再生水补水对热电厂循环冷却水系统的腐蚀影响及控制研究的开题报告.docxVIP

再生水补水对热电厂循环冷却水系统的腐蚀影响及控制研究的开题报告 摘要： 为了解决热电厂循环冷却水系统的水资源问题，再生水补水已成为一种常见的节水措施。然而，再生水中所含有的氯离子、硫酸根离子等成分会引发循环冷却水系统的腐蚀问题，影响循环水质量和系统运行稳定性，给设备和环境带来潜在的安全隐患。 本文旨在研究再生水补水对热电厂循环冷却水系统的腐蚀影响及其控制方法，主要内容包括以下三个方面： 第一部分：概述热电厂循环冷却水系统的腐蚀问题的研究现状和意义，分析再生水补水引发的腐蚀机理和影响因素，提出针对控制再生水补水引发腐蚀的解决方案。 第二部分：选取某热电厂循环冷却水系统作为案例，设计实验研究方法，确定试验样品和试验方案，利用循环水固体表面分析仪、扫描电子显微镜和电化学分析仪等技术手段，定量分析再生水补水对循环冷却水系统腐蚀程度的影响，分析腐蚀产物的成分和结构，从而揭示腐蚀机理。 第三部分：结合实验研究结果，探讨控制再生水补水引发腐蚀的技术措施，包括水源控制、化学处理和物理措施等，提出优化控制策略和工艺方案，提高循环水质量和系统稳定性。 关键词：再生水；循环冷却水系统；腐蚀；控制方案；案例研究。 Abstract: In order to solve the water resource problem of the circulating cooling water system of thermal power plants, the replenishment of reclaimed water has become a common water-saving measure. However, the chlorine ions, sulfate ions and other components contained in the reclaimed water can cause corrosion problems in the circulating cooling water system, affecting the water quality of the circulating water and the stability of the system operation, and bringing potential safety hazards to the equipment and environment. This paper aims to study the corrosion effect of reclaimed water replenishment on the circulating cooling water system of thermal power plants and its control methods. The main content includes the following three aspects: Part I: Overview of the research status and significance of corrosion problems in the circulating cooling water system of thermal power plants, analysis of the corrosion mechanism and influencing factors caused by reclaimed water replenishment, and proposed solution for controlling the corrosion caused by reclaimed water replenishment. Part II: Select a circulating cooling water system of a thermal power plant as a case study, design experimental research methods, determine test samples and test plans, use solid surface analyzers for circulating water, scanning electron microscopy, and electrochemical analyzers and other technical means to quantitatively analyze the influence of reclaimed water replenishment on the degree of corrosi