(2827)--冻融循环作用下再生骨料处理对混凝土性能的影响.pdfVIP

冻融循环作用下再生骨料处理对混凝土性能的影响 摘 要: 本文测试了不同再生粗骨料掺量和再生粗骨料处理的混凝土质量损失率、弹性模量、抗压强度和抗折强度等 1 基本抗冻性能指标，分析了再生粗骨料掺量和骨料处理对混凝土抗冻性能的影响。结果表明： ）再生混凝土的质量 2 和弹性模量损失随再生骨料掺量的增大而增大； ）混凝土的抗冻性能基本呈现出随冻融循环次数的增大而降低的现 象；3）包浆处理可以有效提高混凝土的抗冻性能，整形处理次之，饱水处理再次之。 关键词: 再生骨料 处理方法 冻融循环 再生混凝土 抗冻性能; ; ; ; 中图法分类号:TU528.01 文献标识码:A 文章编号:1000-2324(2019)03-0000-04 Effect of RecycledAggregate Treatment on Concrete Performance underFreeze-thaw Cycle LIU Quan-sheng Henan Vocational Collegeof Water Conservancy andEnvironment,Zhengzhou450008, China Abstract: Concrete samples with different regenerated coarse aggregate content and treatment methods were prepared. The basic antifreeze performance indexes, such as mass loss rate, elastic modulus, compressive strength and flexural strength, were tested. The influence of regenerated coarse aggregate content and treatment on the antifreeze performance of concrete was analyzed.Theresults show that: 1) Themass and elasticmoduluslossofrecycled concreteincreaseswith theincrease of recycled aggregate content. 2) The frost resistance of concrete basically decreases with the increase of freeze-thaw cycle times. 3) Slurry treatment can effectively improve the frost resistance of concrete, followed by plastic treatment and water saturationtreatment. Keywords:Recycled aggregate;treatmentmethod;freeze-thaw cycle;recycledconcrete;antifreezeperformance [1] 建筑施工、旧建筑拆除、装修等均会产生大量的混凝土废料 ，混凝土自身结构稳定，短期内 [2] 难以分解 。废弃混凝土是城市建筑垃圾的重要组成部分，而目前我国总建筑垃圾已经超过200 亿 [3] [4,5] t 。如何处理建筑垃圾已成为环境保护的热点话题 。学者们提出将混凝土废料通过处理作为再生 [6,7] 粗骨料再次浇筑再生混凝土材料，这可以大量消耗建筑垃圾，避免建筑垃圾占用大量土地 。同时， 混凝土通过分拣、破碎、处理和筛分等工序重新加工再次作为再生粗骨料可以有效降低天然粗骨料