(9538)--铝酸盐水泥复合普通硅酸盐水泥对砂浆早期抗冻性能的影响.pdfVIP

铝酸盐水泥复合普通硅酸盐水泥对砂浆 早期抗冻性能的影响 摘要：研究了早期受冻环境下铝酸盐水泥复合普通硅酸盐水泥砂浆试件的力学性能及其微观形貌的变化。结果表明： 纯铝酸盐水泥体系具有良好的早期抗冻性能，但其与普通硅酸盐水泥复合时，普通硅酸盐水泥掺加比例0~70% 时，其 早期抗冻性能会有明显下降趋势；而在70%~100% 时又呈现上升趋势，但增加幅度较小。铝酸盐水泥低掺量掺入会延 迟硅酸盐水泥的水化，导致其复合体系早期抗冻性降低。 关键词：早期受冻；铝酸盐水泥；水泥砂浆；微观结构 Abstract: The mechanical properties and morphology of aluminate cement composite ordinary Portland cement mortars under early freezing conditions were studied. The results showed that the pure aluminate cement system have a good early frost resistance, but when it was mixed with ordinary Portland cement, the early frost resistance of composite cement would obviously decrease when the proportion of ordinary Portland cement was 0~70%. When the proportion of ordinary Portland cement was 70%~100%, the early frost resistance of composite cement would show an upward trend, but the increase was small. The low dosage of aluminate cement would delay the hydration of Portland cement, and lead to the decrease of the early frost resistance of the composite system. Key words: early frost; aluminate cement; cement mortar; microstructure First authors address: College of Materials Science and Engineering, Zhengzhou University, Zhengzhou 450001, Henan, China 中图分类号：TQ172.7　文献标识码：A　文章编号：1002-9877（2019）03-0003-03 0　引言 盐水泥进行复合[3] ，以此来提高水泥基材料的早期强 我国长江以北地区冬季气温低，东北和西北地 度以抵抗早期冻害，但复合的适用性以及在负温环 区在一年中有较长的一段时间处于低温状态，许多 境下的水化进程等需要进行探索。 地区的年负温天气持续时间达到 3~6 个月。混凝土 1　试验材料与方法 的建造以及使用过程受环境影响很大，相比于使用 1.1　原材料 过程中环境对其侵蚀作用的危害，混凝土结构及强 试验中所用普通硅酸盐水泥为新疆天山水泥股 度的形成过程显得至关重要，若在初始阶段不能形 份有限公司生产的P ·O42.5 水泥（OPC）；铝酸盐水泥 成完善的内部结构，后期的环境不利因素对其造成 （CAC）购自河南长城铝业公司，CA50-A700 型，强度 的危害则会成倍地放大，因此有必要对早期受冻环