陶瓷纤维增强摩擦材料的制备及其摩擦磨损机理研究的中期报告.docxVIP

陶瓷纤维增强摩擦材料的制备及其摩擦磨损机理研究的中期报告 摘要： 本研究旨在制备一种具有优异摩擦磨损性能的陶瓷纤维增强摩擦材料，并探究其摩擦磨损机理。采用化学合成和热压成形的方法制备了陶瓷纤维增强Pb-based摩擦材料，并对其进行了摩擦磨损性能测试。 结果表明，陶瓷纤维的加入使得摩擦材料的硬度和抗磨性能得到了明显提升，同时对其摩擦系数和磨损率的影响不明显。通过扫描电镜（SEM）分析，发现陶瓷纤维在材料中的分布均匀，有效地阻碍了摩擦材料的磨损过程。同时，磨损表面上还出现了一些裂纹和局部脱落现象，说明材料的断裂和磨耗是同时发生的。 结论：陶瓷纤维增强摩擦材料具有优异的摩擦磨损性能，陶瓷纤维的加入能够有效地提高材料的硬度和抗磨性能，防止材料的过度磨损和失效。同时，这种材料的断裂和磨耗是同时发生的，对其磨损机理需要进一步研究。 Abstract: The aim of this study was to prepare a ceramic fiber-reinforced friction material with excellent friction and wear properties and to explore its friction and wear mechanism. Pb-based friction material reinforced with ceramic fibers was prepared by chemical synthesis and hot-pressing, and its friction and wear properties were evaluated. The results showed that the addition of ceramic fibers led to a significant increase in the hardness and wear resistance of the friction material, while its friction coefficient and wear rate were not significantly affected. Scanning electron microscopy (SEM) analysis showed that the distribution of ceramic fibers in the material was uniform, effectively preventing the wear process of the friction material. At the same time, there were some cracks and local shedding on the wear surface, indicating that the fracture and wear of the material occurred simultaneously. Conclusion: Ceramic fiber-reinforced friction material has excellent friction and wear properties. The addition of ceramic fibers can effectively improve the hardness and wear resistance of the material, prevent excessive wear and failure of the material. At the same time, the fracture and wear of this material occur simultaneously, and its wear mechanism needs further study.