二组分固液相图的绘制.docVIP

实验报告纸

表-1

t/min

T/℃

纯铅

锡20%

锡40%

锡61.9%

锡80%

纯锡

0

395.4

395.3

397.5

398.7

399.3

394.5

1

385.3

387.0

396.8

385.3

391.3

384.9

2

374.4

378.5

396.6

375.0

383.5

375.5

3

365.3

369.8

367.3

365.1

375.0

365.7

4

355.2

363.5

353.8

354.6

367.8

357.9

5

346.8

356.9

345.0

346.2

359.8

350.0

6

338.7

348.8

335.1

336.9

353.1

341.8

7

329.6

342.1

327.2

329.6

346.7

334.5

8

322.9

335.8

319.5

322.6

339.6

327.6

9

317.8

328.8

311.5

315.4

333.9

320.8

10

311.8

323.2

305.2

309.3

327.3

314.8

11

306.6

316.2

298.6

303.6

321.1

307.2

12

302.2

311.8

293.2

297.3

315.8

302.5

13

298.6

307.2

288.1

292.0

311.0

296.3

14

294.4

302.5

282.1

286.6

306.4

291.2

15

288.7

298.9

276.8

285.0

302.2

286.1

16

283.4

295.3

271.2

275.2

297.4

280.4

17

277.9

291.1

264.8

269.3

293.0

275.5

18

270.6

287.3

259.4

264.4

288.5

271.1

19

264.0

282.3

254.5

257.7

283.3

266.5

20

256.8

277.5

248.9

254.4

278.6

261.7

21

250.8

272.2

244.3

250.2

273.5

257.6

22

245.3

266.2

239.3

245.8

269.3

252.9

23

239.2

261.3

235.1

241.3

265.1

249.2

24

234.5

256.7

231.0

237.4

260.5

245.3

25

230.0

252.0

226.5

233.0

256.6

241.1

26

225.1

247.9

222.7

229.4

252.9

237.6

27

221.0

244.2

219.0

225.9

248.8

233.8

28

217.1

240.3

215.0

221.9

245.3

230.5

29

212.7

236.7

211.5

218.7

241.1

227.2

30

209.1

232.6

208.2

215.4

238.7

223.7

31

205.6

229.2

204.5

211.9

234.9

220.9

32

201.7

225.7

201.5

209.6

231.2

224.5

33

198.1

221.9

198.1

209.4

228.3

230.6

34

194.7

218.7

195.4

208.1

225.3

231.1

35

191.7

215.0

192.9

206.7

222.0

231.1

36

188.7

212.0

190.3

204.9

219.3

230.9

实验报告纸

37

185.2

209.0

188.6

203.0

216.5

230.5

38

182.4

206.1

185.9

200.8

218.9

229.7

39

179.7

202.8

183.3

198.6

221.4

221.4

40

176.5

200.1

181.1

197.3

221.0

216.3

41

173.9

196.9

179.1

195.0

219.7

210.4

42

170.9

194.4

181.1

192.4

218.1

205.7

43

168.3

191.7

183.2

190.0

215.8

202.7

44

165.9

188.5

183.6

187.8

214.7

199.0

45

163.1

186.7

183.0

185.5

211.7

196.0

46

160.8

184.5

180.2

183.8

208.8

193.0

47

158.5

182.1

175.3

182.2

206.2

190.2

48

155.8

180.2

171.9

181.4

203.1

188.1

49

153.7

178.4

168.7

180.0

200.3

185