FeB-Q235及B4C-QT500-7复合材料耐磨性研究的开题报告.docxVIP

FeB-Q235及B4C-QT500-7复合材料耐磨性研究的开题报告

(Title)AStudyontheWearResistanceofFeB-Q235andB4C-QT500-7Composites

(Background)Invariousindustrialapplications,materialswithhighwearresistancearerequiredtoextendthelifespanofmachineryandequipment.Metalmatrixcomposites(MMCs),whicharecomposedofametallicmatrixandareinforcingmaterial,haveshowngreatpotentialforenhancingwearresistance.

(Objectives)TheaimofthisstudyistoinvestigatethewearresistanceofFeB-Q235andB4C-QT500-7compositesunderdifferentconditions.Specificobjectivesareasfollows:

1.TofabricateFeB-Q235andB4C-QT500-7compositesusingpowdermetallurgy(PM)technique.

2.Tocharacterizethemicrostructureandmechanicalpropertiesofthecomposites.

3.Toevaluatethewearresistanceofthecompositesusingpin-on-disctestunderdifferentloadsandslidingspeeds.

4.Toanalyzethewearmechanismsofthecompositesandcomparetheirperformances.

(Methods)TheFeB-Q235andB4C-QT500-7compositeswillbefabricatedusingPMtechnique,whichinvolvesmixingthepowdersofmatrixandreinforcingmaterials,compactingthem,andsinteringathightemperature.Themicrostructureandmechanicalpropertiesofthecompositeswillbecharacterizedusingscanningelectronmicroscope(SEM),X-raydiffraction(XRD),andmechanicaltesting.Thewearresistanceofthecompositeswillbeevaluatedusingpin-on-disctest,wherearotatingpinslidesagainstastationarydiscunderaspecificloadandslidingspeed.TheweartrackwillbeexaminedusingSEMtoidentifythewearmechanismsandquantifythewearrate.

(Expectedoutcomes)ItisexpectedthatFeB-Q235andB4C-QT500-7compositeswillhavesuperiorwearresistancecomparedtotheirindividualcomponents.Thewearmechanismsofthecompositeswillbeidentified,andtheeffectofloadandslidingspeedonthewearratewillbeanalyzed.TheoutcomesofthisstudywillprovideinsightsontheapplicationofMMCs