有机硅改性丙烯酸酯乳液的合成和形态分析

严微;鲁琴;胡荣涛;杨婷婷;高庆;彭慧;程时远

【摘要】Methylmethactylate(MMA)/butylacrylate(BA)/vinylterminalpolysiloxane(Si-1800)emulsionwaspreparedusingammoniumpersulfate(APS)asinitiator,sodiumdodylcylbenzenes-ulfonate(SDBS)/sodium(polyoxyethylatedoctylphenol)maleate(OP-10)ascompoundemulsifier.Themorphologyofemulsionwasobservedbytransmissionelectronmicroscropy(TEM).Ithadbeenfoundthatthebeststainingmethodwasbyphosphotungsticacid(PTA)atpHvalue2.0.Underabovecondition,theparticlesizewasverifiedincreasingwiththeinitiatoramountassistedbyphotoncorrelationspectroscopy(PCS).ThesizedistributionofthelatexparticleswasevenatthebestSDBSandOP-10ratioof1:2andthebest

Si-1800contentof9%.ItalsoprovedthatthemicellarnucleationmechanismtookeffectduringthepolymerizationcourseofMMA/BA/?Si-1800bytrackingthechangeofparticlesizewithreactiontimeatdifferentSi-1800contents.%以过硫酸铵(APS)为引发剂、十二烷基苯磺酸钠(SDBS)/辛基酚聚氧乙烯醚马来酸酯钠(OP-10)为复合乳化剂,利用含乙烯基的有机硅单体与丙烯酸酯类单体进行乳液聚合制备了甲基丙烯酸甲酯(MMA)/丙烯酸丁酯(BA)/有机硅(Si-1800)交联聚合物乳液.通过透射电子显微镜(TEM)观察乳胶粒形态的最佳染色方法为pH-2.0的PTA染色.在此条件下采用先子相关光谱(PCS)法通过激光光散射粒度仪测试发现乳胶粒的粒径随着引发剂用量的增加而增大;在SDBS和OP-10配比为1:2、Si-1800含量为9％的最佳条件下,乳胶粒粒径分布均匀;通过跟踪不同

Si-1800含量下乳胶粒粒径随反应时间的变化确定MMA/BA/Si-1800复合乳液的

成核机理以胶束成核为主.

【期刊名称】《化学与生物工程》

【年(卷),期】2011(028)008

【总页数】5页(P24-28)

【关键词】丙烯酸酯;有机硅;乳胶粒;形态

【作者】严微;鲁琴;胡荣涛;杨婷婷;高庆;彭慧;程时远

【作者单位】湖北大学材料科学与工程学院功能材料绿色制备与应用省部共建教育部重点实验室,湖北武汉430062;武汉华工图像技术开发有限公司,湖北武汉430223;武汉荟普化学新材料有限公司,湖北武汉430030;湖北大学材料科学与工程学院功能材料绿色制备与应用省部共建教育部重点实验室,湖北武汉430062;湖北大学材料科学与工程学院功能材料绿色制备与应用省部共建教育部重点实验室,湖北武汉430062;湖北大学材料科学与工程学院功能材料绿色制备与应用省部共建教育部重点实验室,湖北武汉430062;湖北大学材料科学与工程学院功能材料绿色制备与应用省部共建教育部重点实验室,湖北武汉430062

【正文语种】中文

【中图分类】O627.4;O631.5

在众多的高分子材料中，丙烯酸酯聚合物由于具有优良的耐候性、耐(臭)氧性、耐油性、附着力，以及单体众多、合成容易、价格便宜等优点而得到广泛的应用。但是，丙烯酸酯聚合物的耐温性、耐水性、透气性较差，限制了它的进一步应用[1，

2]。

有机硅在高分子材料科学中有着极为重要的作用[3，4]。有机硅单体及其聚合物具有极低的表面能，Si-O键具有很高的键能，键旋转容易。这些特性赋予其优良的耐水性、耐高低温性、耐候性、透气性。用有机硅对丙烯酸酯