材料力学实验报告标准答案.doc

力学实验报告

标准答案

长安大学力学实验教学中心

目录

拉伸实验···············································································2

压缩实验···············································································4

拉压弹性模量E测定实验···················································6

四、低碳钢剪切弹性模量G测定实验·······································8

五、扭转破坏实验····································································10

六、纯弯曲梁正应力实验··························································12

七、弯扭组合变形时的主应力测定实验··································15

八、压杆稳定实验······································································18

一、拉伸实验报告标准答案

实验目的：

见教材。

实验仪器

见教材。

实验结果及数据解决：

例:(一)低碳钢试件

试验前

试验后

最小平均直径d=10.14mm

最小直径d=5.70mm

截面面积A=80.71mm2

截面面积A1=25.50

计算长度L=100mm

计算长度L1=133.24mm

实验前草图

实验后草图

强度指标:

Ps=__22.1___KN屈服应力σs=Ps/A__273.8___MPa

Pb=__33.2___KN强度极限σb=Pb/A__411.3___MPa

塑性指标:

33.24%68.40%

低碳钢拉伸图:

（二）铸铁试件

试验前

试验后

最小平均直径d=10.16mm

最小直径d=10.15mm

截面面积A=81.03mm2

截面面积A1=80.91mm2

计算长度L=100mm

计算长度L1≈100mm

实验前草图

实验后草图

强度指标:

最大载荷Pb=__14.4___KN

强度极限σb=Pb/A=_177.7__MPa

问题讨论：

为什么在拉伸实验中必须采用标准试件或比例试件,材料相同而长短不同的试件延伸率是否相同?

答:拉伸实验中延伸率的大小与材料有关,同时与试件的标距长度有关.试件局部变形较大的断口部分,在不同长度的标距中所占比例也不同.因此拉伸实验中必须采用标准试件或比例试件,这样其有关性质才具可比性.

材料相同而长短不同的试件通常情况下延伸率是不同的(横截面面积与长度存在某种特殊比例关系除外).

分析比较两种材料在拉伸时的力学性能及断口特性.

答:试件在拉伸时铸铁延伸率小表现为脆性,低碳钢延伸率大表现为塑性;低碳钢具有屈服现象,铸铁无.低碳钢断口为直径缩小的杯锥状,且有450的剪切唇，断口组织为暗灰色纤维状组织。铸铁断口为横断面，为闪光的结晶状组织。.

教师签字:________

日期:________

二、压缩实验报告标准答案

实验目的：

见教材。

实验原理：

见教材。

实验数据记录及解决：

例：(一)实验记录及计算结果

材料

低碳钢

铸铁

试件尺寸

直径d=_15__mm

长度L=____20____mm

面积A=__176.63_mm2

直径d=__15____mm

长度L=___20_____mm

面积A=__176.63_mm2

试件形状草图

实验前

实验后

屈服载荷

屈服应力

Ps=___49_____KN

σs=____277.4__MPa

最大载荷

抗压强度

Pb=___153__KN

σb=__866.2__MPa

问题讨论：

1、分