相分离法制备多孔聚甲基丙烯酸甲酯（PMMA）微胶囊.docxVIP

相分离法制备多孔聚甲基丙烯酸甲酯（PMMA）微胶囊

王建平;李丹;康召青;高阳;李伟;王学晨;张兴祥

【摘要】N-isopropylacrylamidepolymer(PNIPAm)asthermosensitivepore-foamingagentwasintroducedintothesystemforthesynthesisofporouscore-shellmicrocapsulesbyinternalphaseseparation.Thesystemiscomposedofn-octadecane(n-Oct),methylmethacrylate(MMA)andsodiumsaltofstyrene-maleicanhydridecopolymer(SMA)aqueoussolutionformingamicroemulsion.TheeffectofPNIPAmontheformationmechanism,surfacemorpholo-gies,andthermalstabilitiesoftheMicroPCMswasstudiedbyusingFouriertransforminfraredspectroscopy(FTIR),scanningelectronmicroscopy(SEM),differentialscanningcalorimetry(DSC),andthermogravimetricanalysis(TG),respectively.TheresultsindicatethataddingPNIPAmintothesystem,theresultingmicrocap-suleshavesomeirregularholesonthecapsuleshell.Thesizeofthemicrocapsulesisintherangeof2.0-4.0μm.ThenumberofholesincreaseswiththeadditionofPNIPAm,whentheadditionamountof0.3-1.2g.Atthesametime,thenumberoftheholesdecreaseswiththeincreaseofthemolecularweightofPNIPAmandthecontentofMMA,soonlythePNIPAmwithsmallmolecularweightconducivetothesynthesisofporousmicrocapsules.%以具有温敏性的线性聚N-异丙基丙烯酰胺（PNIPAm）为致孔剂，在十八烷（n-Oct）/甲基丙烯酸甲酯（MMA）/苯乙烯马来酸酐共聚物钠盐（SMA）水溶液微乳液体系中用相分离法制得包覆有n-Oct的多孔聚甲基丙烯酸甲酯（PMMA）微胶囊，采用扫描电子显微镜（SEM）、差示扫描量热仪（DSC）、热重分析仪（TG）等手段分别考察了这种多孔PMMA微胶囊.实验结果表明：所得多孔微胶囊粒径在2.0~4.0μm，呈多孔微球状，当PNIPAm的添加质量为0.3~1.2g时，多孔PMMA微胶囊表面孔隙数量稍有增加，而当增加MMA的用量或者增加PNIPAm相对分子质量时，多孔PMMA微胶囊表面孔隙数量下降.

【期刊名称】《天津工业大学学报》

【年(卷),期】2016(035)003

【总页数】6页(P39-44)

【关键词】聚N-异丙基丙烯酰胺;相分离法;多孔PMMA微胶囊

【作者】王建平;李丹;康召青;高阳;李伟;王学晨;张兴祥

【作者单位】天津工业大学天津市先进纤维与储能技术重点实验室，天津300387;天津工业大学天津市先进纤维与储能技术重点实验室，天津300387;天津工业大学天津市先进纤维与储能技术重点实验室，天津300387;天津工业大学天津市先进纤维与储能技术重点实验室，天津300387;天津工业大学天津市先进纤维与储能技术重点实验室，天津300387;天津工业大学天津市先进纤维与储能技术重点实验室，天津300387;天津工业大学天津市先进纤维与储能技术重点实验室，天津300387

【正文语种】中文

【中图分类】TQ31;O63

聚合物相分离法制备微胶囊主要包括2个途径：聚合导致相分离法和溶剂蒸发法.聚合导致相分离法实质是利用了溶解有单体的