大掺量粉煤灰混凝土早龄期力学性能.pdfVIP

大掺量粉煤灰混凝土早龄期力学性能研究

[摘要]通过分析在变温养护条件下大掺量粉煤灰混凝土的早龄

期时抗压强度、抗折强度和劈裂抗拉强度及三点抗弯荷载应力挠度

关系曲线等力学性能指标，同时讨论了等效龄期与早龄期抗压强度

的关系。研究结果表明：大掺量粉煤灰的力学性能在模拟的实际结

构的变温条件下养护比在标准条件下养护有明显的提高。

[关键词]混凝土，粉煤灰，力学性能，养护温度

earlyagemechanicalpropertiesofthehighvolumeflyash

concrete

gaojihong

(chinaoceanengineeringconstructiongeneral

bureau,dalian,116024)

abstractthispaperpresentsastudyonthehighvolumefly

ash(hvfa)concretewhichwascuredinthesimulated

conditionsinrealstructuresandinstandardcondition

mechanicalproperties.theirearlyagemechanical

characteristicsincludedthecompressivestrength,flexural

strengthandsplitting-tensilestrengths,weremeasuredfrom

thetimeofsettingtill7day.thetemperatureinthecuring

chamberchangescontinuouslyaccordingtotheadiabatic

temperaturerisingcurve.equivalentagebasedonthe

apparentactivationenergyisintroducedtounderstandthe

progressofearlyagemechanicalpropertiesofvariable

temperaturecuringconcrete

1前言

目前，可持续发展成为社会倍受关注的热点，混凝土材料作为

主要的建筑材料，其对环境的影响日益受到人们的重视。大掺量粉

煤灰混凝土被认为是绿色混凝土[1][2]，成为研究的热点之一。大

掺量粉煤灰混凝土早龄期阶段的力学性能直接影响其在工程中的

应用[3]。本文研究在正常的养护制度和模拟实际结构中混凝土温

度变化一般规律的变温养护条件下分析在掺量粉煤灰混凝土早龄

期时抗压强度、抗折强度和劈裂抗拉强度等力学指标。

2实验

2.1原料

水泥为大连小野田水泥有限公司生产的普通硅酸盐水泥

po42.5，粉煤灰为辽宁抚顺一级粉煤灰，高效减水剂为大连建筑科

学研究院外加剂公司生产的聚羧酸高效水剂sk3301。砂为河砂细度

模数3.0，石子为大连石灰石矿产青碎石，级配5-20mm。原料化学

成分如表1所示。混凝土配合比按jgj55-2000《普通混凝土配合比

设计规程》设计，具体结果如表2所示。

表1原材料的化学组成（质量%）

原料sio2al2o3caofe2o3mgok2ona2omno2

so3loi

水泥22.804.5565.342.822.740.520.25-

2.923.97

粉煤灰58.0923.692.997.201.321.333.18-

-1.14

表2混凝土配合比

编号硅酸盐水泥

kg/m3粉煤灰

kg/m3砂

kg/m3石子

kg/m3用水量

kg/m3高效减水剂