_磷含量及热处理对化学镀镍磷合金硬度的影响.pdfVIP

DOI:10.14158/ki.1001-3814.2013.16.019

磷含量及热处理对化学镀镍磷合金硬度的影响

段海龙,傅强,钟毅

(昆明理工大学材料科学与工程学院,云南昆明650093)

摘要：采用在铝合金基体上酸性化学镀镍，研究了镍磷镀层中磷含量及热处理温度对镀层硬度的影响。结果发

现，镀层的硬度随磷含量的增大而增大；在一定温度范围内，随热处理温度的升高，硬度随之增加。

关键词：磷含量；热处理；硬度

中图分类号：G166.7文献标识码：文章编号：3814(2013)16-0138-02

TA1001-

InfluenceofPhosphorusContentandHeatTreatmentonHardnessof

ElectrolessNi-PAlloy

DUANHailong,FUQiang,ZHONGYi

(FacultyofMaterialsScienceandEngineering,KunmingUniversityofScienceandTechnology,Kunming650093,China)

：

AbstractWiththemethodofaluminumalloysubstrateacidchemicalnickelplating,theeffectsofphosphoruscontentin

theNi-Pcoatingandheattreatmenttemperatureonthehardnessofcoatingwerestudied.Theresultsshowthatthephosphorus

contentandtheheattreatmenttemperaturehavegreatinfluenceonthehardnessofthecoating.Withphosphoruscontent

increasing,thehardnessincreases,while,inacertaintemperaturerange,withtheincreaseoftheheattreatmenttemperature,

thehardnessincreases.

：phoruscontent;heattreatment;hardness

Keywordsphos

化学镀镍磷合金作为功能镀层日益受到社会各试样需要对其用线切割从中间切开，再用苛性钠溶

行业的重视，在很多领域得到了运用[1-3]。采用电镀液溶解掉铝基体，得到镀层样品。

和化学镀方法可以提高铝及铝合金的表面硬度、耐1.2硬度及磷含量的测定

磨性能和耐腐蚀性能，其中铝基化学镀镍磷合金技实验采用维氏显微硬度对试样进行硬度测试。每