六种模具钢对比

化学成分

CSiMnCrMoWVNb其他

Cr12Mo1V11.40~1.60≤0.60≤0.6011.00~13.00.70~1.20-≤1.10-Co≤1.00

0P≤0.030

S≤0.030

Cr12MoV1.45~1.70≤0.40≤0.4011.00~12.50.40~0.60-0.15~0.30-P≤0.030

0S≤0.030

RM20.40~0.50≤0.40≤0.403.4~4.41.5~2.14.5~5.30.70~1.1-P≤0.030

S≤0.030

LD0.70~0.800.70~1.0.20~06.50~7.502.00~3.00-1.70~2.20-P≤0.030

20.50S≤0.030

65Nb0.60~0.70≤0.35≤0.403.8~4.42.0~2.52.5~3.00.8~1.10.20~0.30P≤0.035

S≤0.035

65420.80~0.900.20~0.0.15~03.80~4.404.50~5.505.50~6.1.75~2.20P≤0.030

45.4075S≤0.030

性能及热处理工艺

Cr12Mo1V1Cr12MoV65NbLDRM2(5Cr4W5Mo2V)W6Mo5Cr4V2

热处理工艺1050℃油淬，1020℃油1120℃油1100油淬，1130℃油淬，630℃

1180℃油冷，

200℃回火淬，200℃回淬，550℃550℃回火回火

560℃回火

火回火

硬度HRC60~6560~6159~6361~6246~5062.5~66