7XXX铝合金弹壳外表面残余应力分析

江长友，金辉，陈露

(重庆嘉陵特种装备有限公司，重庆400032)

摘要：利用X射线衍射法对不同加工状态的7XXX高强度铝合金弹壳的外表面残余应力进行了系统分析。结果表

明：不同引长和收口状态的弹壳经退火处理后，能有效减少残余应力；固溶/时效处理后，收口部位和底部的残余应力

明显增大，表面残余应力总的表现比未时效的有所提高。

关键词：7XXX铝合金；残余应力；X射线衍射法；弹壳

DOI:10.14158/j.cnki.1001-3814.

中图分类号：TG166.3文献标识码：A文章编号：1001-3814(2021)12-0132-03

AnalysisonResidualStressonExternalSurface

of7XXXAluminumAlloyShellCase

JIANGChangyou,JINHui,CHENLu

(ChongqingJialingSpecialEquipmentCo.,Ltd.,Chongqing400032,China)

Abstract：Theresidualstressontheoutersurfaceof7XXXhighstrengthaluminumalloyshellcasewithdifferent

processingstateswassystematicallyanalyzedbyX-raydiffractionmethod.Theresultsshowthattheresidualstressoftheshell

casewithdifferentelongationandclosingstatecanbeeffectivelyreducedafterannealing.Aftersolidsolution/agingtreatment,

theresidualstressatthemouthandbottomincreasesobviously.Theoveralperformanceofsurfaceresidualstressishigher

thanthatofwithoutaging.

Keywords：7XXXaluminiumalloy;residualstress;X-raydiffractionmethod;shellcase

目前，国内弹壳材料以钢材和铜材为主，这两种的残余应力进行分析。

材料的密度高，制造的弹壳重量较重，这严重制约了本文采用X射线衍射法对铝合金弹壳底部、中

战士在战场上的枪弹携带量。研究枪弹的减重，尤其部和收口薄壁锥形过渡区等典型部位进行残余应力

是枪弹壳的减重具有重要意义，因为弹壳的质量几