时效处理对CuMoCr合金硬度及导电率的影响.pdfVIP

HotWorkingTechnology2014，Vo1．43，No．10

时效处理对CuMoCr合金硬度及导电率的影响

赵月红．李会新。赵文蕾

(秦皇岛职业技术学院机电工程系，河北秦皇岛066100)

摘要：测试了时效处理前后CuMoCr合金的硬度及导电率，探讨了时效处理对CuMoCr合金硬度及导电率的影

响。结果表明：时效处理能改变CuMoCr合金的硬度和导电率，当该合金经500℃保温4h时效后可获得较高硬度和导

电率，其值分别为227HV和24．6MS／m。

关键词：CuMoCr合金；时效处理；硬度；导电率

中图分类号：TG146．11文献标识码：A文章编号：1001．3814(2014)10．0108．02

EffectofAgingTreatmentonHardnessandElectricalConductivity

ofCuMoCrAlloy

ZHAOYuehong，LIHuixin，ZHAOWenlei

(DepartmentofElectromechanicalEngineering，QinhuangdaoVocationalTechnologicalCollege，Qinhuangdao066100，

Chnia)

Abstract：ThehardnessandelectricalconductivityofCuMoCralloybeforeandafteragingtreatmentweremeasured，

andtheeffectofagingrteatmentonthehardnessandelectricalconductiviytofthealloywerestudied．Theresultsshowthat

agnigrteamtentcanchangehteharndessandelectricalconductiviytofthealloy．Thelragerhardnessandelectrical

conductivityofthealloyCnabeobtainedbyagingrteatmentat500℃for4h．Thehrandessandelectricalconductiviytis

227HVand24．6MS／m，respectively．

Keywords：CuMoCralloy；agingrteamtent；hradness；electricalconductivity

CuCr合金具有较好耐高温强度和优良导电性，

已作为触头材料在真空断路器中得到广泛应用ll-2]。

1实验材料及方法

然而CuCr触头材料中的Cr相为电击穿弱相圈，粗大

Cr枝晶的存在将降低CuCr合金的耐电压强度。随着材料为凝固态CuMoCr合金，其化学成分(质量

城网和农网改造的进行，对大功率真空断路器的需分数，％)为62．99Cu、27．26Mo、9．52Cr、其余0．23。样

求量越来越大，同时对触头材料性能也提出更高的品尺寸为10mmx10mm×5rnrll，在KL．13D型箱式

要求。因此，开发研制高性能的触头材料具有一定电阻炉中分别进行200、300、400、500、600℃保温

的实际意义。据文献报道[4—5]，往CuCr合金中添加4h的时效处理。

W、Ni、A1、Co等合金元素，在不改变制备工艺条件时效处理前后试样经1200砂纸打磨及抛光

下。可提高合金的耐电压强度及电性能。由于钼与后：用HVS．1000型显微硬度计和WD．Z型涡流电

铬相比，具有较高