固相烧结低钨含量W-Ni-Fe合金的微观结构与力学性能.docxVIP

固相烧结低钨含量W-Ni-Fe合金的微观结构与力学性能

徐欢;曹顺华;陈炳煌;肖彬;李世康

【摘要】采用固相烧结工艺(1300℃保温1h)制备低钨含量(质量分数为60%~80%)的W-Ni-Fe合金，测定合金的抗拉强度、抗压强度和伸长率，利用金相显微镜观察合金的显微组织，并通过扫描电镜(SEM)观察合金断口形貌，研究钨含量对固相烧结W-Ni-Fe合金力学性能与微观结构的影响。结果表明：随钨含量降低，合金的孔隙率和平均孔径减小，抗拉强度增大，伸长率显著提高，抗压强度变化不大。W含量为60%~80%的W-Ni-Fe合金，其孔隙率为17.8%~21.4%，抗拉强度为231~262MPa，抗压强度2450~2550MPa，伸长率为0.3%~2.3%，压拉比为9.45~11.04，都能满足易碎型穿甲弹弹芯材料的性能要求。%W-Ni-Fealloyswithlowtungstencontent(60%?80%,massfraction)werepreparedbysolidstatesintering.Themechanicalpropertiesincludingtensilestrength,compressionstrengthandelongationofthesampleweretested.Themicrostructureandfracturemorphologywereinvestigatedbyscanningelectronmicroscopy(SEM).TheeffectsoftungstencontentonmechanicalpropertiesandmicrostructureofW-Ni-Fealloysaftersolidstatesinteringwerealsostudied.Theresultsshowthat,withdecreasingtungstencontent,theporosityandaverageporesizeofalloysdecrease,tensilestrengthincreases,elongationincreasessignificantly,andcompressionstrengthchangesalittle.TheW-Ni-Fealloyswithtungstencontentintherangeof60%?80%haveporosityof17.8%?21.4%,tensilestrengthof231?262MPa,compressivestrengthof2450?2550MPa,elongationof0.3%?2.3%,andtheproportionofcompressivestrengthandtensilestrengthof9.45?11.04,whichallmeettherequirementsofthefragilearmour-piercingprojectile.

【期刊名称】《粉末冶金材料科学与工程》

【年(卷),期】2016(021)003

【总页数】6页(P383-388)

【关键词】钨合金;低钨含量;固相烧结;力学性能;断口形貌

【作者】徐欢;曹顺华;陈炳煌;肖彬;李世康

【作者单位】中南大学粉末冶金国家重点实验室，长沙410083;中南大学粉末冶金国家重点实验室，长沙410083;中南大学粉末冶金国家重点实验室，长沙410083;中南大学粉末冶金国家重点实验室，长沙410083;中南大学粉末冶金国家重点实验室，长沙410083

【正文语种】中文

【中图分类】TF125

钨合金具有密度高、强度高、塑性强等优良性能，是目前制备动能穿甲弹的主要材料[1]。相对于榴弹来说，传统钨合金动能穿甲弹具有较强的轴向破坏特性，但对目标没有较好的杀伤效果。为提高穿甲弹的杀伤能力，研究人员提出并制备了一种新型的易碎性钨合金穿甲弹[2?4]，这种钨合金穿甲弹具有一定的穿甲能力，同时又能够造成较大的杀伤效果。易碎性穿甲弹要求弹芯材料拥有一定的脆性，能够在穿甲过程中碎裂成若干碎片[4]。为了能够破碎成理想的破片，钨合金应具有较低的抗拉强度。同时为保证发射强度又需要足够的抗压强度及伸长率，即保证一定塑性的前提下，有较大的压拉比。根据W-Ni-Fe合金的脆裂机理[5]，国内外已研制出多种易碎钨合金[4,6]，然而多数易碎钨合金如W-Ni-Fe(Al2O