沥青路面施工离析解决方法.docVIP

沥青路面施工过程中离析现象的成因及解决方法探讨　摘要本文通过对沥青路面施工时出现离析现象的原因、危害的分析，从3个方面提出了减少离析现象及消除其产生后果的方法。　关键词离析现象沥青混凝土摊铺平整度 Discussion on the Forming Causes of Formation of Resolution Phenomenon and Its Solving Methods in the Construction Course on Bituminous Road SurfaceWang Hao(2th Highway Engineering Bureau 4th Engineering Department of Communications Ministry) 　AbstractThis paper through the analysis of the causes and injury of arised resolution phenomenon for the construction course on bituminous road surface，raises the methods of reducing resolution phenomenon and eliminating its consequence from three aspects.　Key wordsResolution phenomenonBituminous concrete Spread Planeness 　　1工程概况　　本工程属宁(南京)-连(连云港)平原微丘区一级公路，路线全长286km。设计行车速度100km ／h。路基宽度24.50m，其中中间带3.0m(含路缘带2×0.5m)，行车道为2×3.75m，硬路肩为 2×2.5m(含路缘带2×0.5m)，土路肩2×0.75m。其中淮阳市境K78＋400～K98＋143段由交通 部第二公路工程局第四工程处承建。1.1行车道及路缘带路面结构　　采用沥青混凝土路面，即4cm中粒式沥青混凝土抗滑层＋5cm粗粒式沥青混凝土＋6cm热拌沥青碎石＋1cm砂粒式沥青混凝土，基层采用二灰碎石，底基层采用二灰上。1.2沥青路面面层配合比设计　　宁连路K78＋400～K98＋143段沥青路面面层，AC-16Ⅱ、AC-30Ⅰ、AM-30、AC-5Ⅰ沥青混凝土配合比设计是根据《公路沥青路面施工技术规范》(JTJ032-94)进行设计的，其中试验是根据《公路沥青及沥青混合料试验规程》(JTJ052-93)和《公路工程集料试验规程》(TJT058-94)进行的。沥青新加坡70#重交通沥青用于AC-16Ⅱ中粒式沥青混凝土，克拉马依70#重交通沥青用于AC-SOI粗粒式沥青混凝土，AM-30沥青碎石，AC-5Ⅰ砂粒式沥青混凝土。矿料采用：碎石采用大石山通宇公司生产的1-3碎石，瓜子片(0.5～1.5)，米砂(0.2～0.7)；黄砂采用新沂产的河砂；矿粉采用洪泽水泥厂的矿粉。　　AC-16Ⅱ中粒式沥青混凝土级配如下：　　　　2问题的提出　　1996年3月18日至23日，我们在K87＋400～K87＋750段施工时，发现在沥青碎石铺筑时沥青混合料出现严重离析现象，其离析位置具有规律性，如图1所示。于是我们把该段做为试验路段，对其进行了专门的分析研究，并探索出了具体解决办法。　3研究过程3.1沥青碎石形成离析带的原因　　根据现场离析带形成的状况与特点，我们发现沥青碎石形成离析带主要有以下几个方面的原因：　　(1)沥青混合料从贮料罐向运输车里输送时，由于高度原因，大骨料滚落在车厢附近，形成粗集料第一次集中。　　(2)运输车里的混合料卸向摊铺机时，大骨料滚落在摊铺机半厢附近，形成粗集料的第二次集中。　　(3)摊铺机送料器在送料过程中，先将中间集料送于布料器，剩余粗集料留存在料斗中，摊铺机收斗时，形成粗集料的第三次集中。　　3.2沥青碎石离析的危害　　(1)沥青碎石粗集料一旦形成集中，在碾压过程中，集料非常容易被压碎，骨料表面积增大，改变了原设计的路面配合比，油料偏少，造成集料碾压成型后松散，破坏路面结构，影响路面强度、行车安全和行车效果以及道路使用寿命。　　(2)粗集料集中，局部密实度差，孔隙率高，容易在路面形成积水，影响路面质量。　　(3)粗集料集中，影响路面平整度及路面外观美感。3.3解决沥青碎石形成离析带方法　　为解决沥青混合料出现规律性离析现象，我们在研究中从以下几个方面进行控制和解决。　3.3.1从运输车辆方面来解决　　(1)从拌和