提升高 RH 循环流量的工艺研究 1 1 1 1 1 2 常立山 姚瑞凤 马连昌 李太全 王淑满 程迪 （1.邯郸钢铁集团邯宝炼钢厂；2.邯郸钢铁集团技术中心，邯郸 056015 ） 摘 要 本文对邯钢 250t 钢包 RH 真空精炼过程进行相似比为 1/4 的水模型实验，研究了不同环流气量时对钢水循 环流量的影响，确定合理的环流气量为 2000L/min 至 3000L/min 。在生产中比较真空处理下不同环流气量时钢水不 同时间段的含氢量变化，总结RH 生产中钢水循环流量的影响。 关键词 RH 精炼 环流气量 循环流量 水模拟 Research of Improving Circulation Flow Rate in RH Chang Lishan1 Yao Ruifeng1 Ma Lianchang1 Li Taiquan1 Wang Shuman1 Cheng Di2 （1. Handan Iron Steel (Group) Corporation Hanbao Steel Plant;2. Hebei Handan Iron Steel Group Co.,Ltd. Technological Center, Handan, 056015 ） Abstract This text is water model of similar ratio 1/4 in 250t RH vacuum refining process in Handan Iron and Steel Co., the circulation flow rate has been investigated for different circumfluence gas flux, it was found that the reasonable circumfluence gas flux were from 2000L/min to 3000L/min. The content of hydrogen was been analyzed for different circumfluence gas flux and time distance in production process, the influence of circumfluence gas flux on steel circulation effect was summarized in RH produce process. Key words RH refining, circumfluence gas flux, circulation flow rate, water simulation 1 引言 近年来冶金工业发展迅速，对钢材质量的要求越来越高，高品质钢的需求量也在不断增加。在这种形势 下，RH 多功能精炼炉体现了其至关重要的精炼地位，发挥了独特的冶金效果，因此RH 精炼工艺在学术研 究领域和生产实践领域都进一步得到了提高和完善。 本文以邯钢 250tRH精炼装置的主要工艺参数为基础，通过相似比，模拟RH装置内的浸渍管插入深度、 环流气量和循环流量的变化情况。当RH装置内的环流气量加大，真空处理时间延长，则钢水的循环流量增 加，脱氢能力加强[1] 。因此在生产过程中，选取RH真空处理时间、环流气量以及定氢值来分析钢水循环流 量的变化。 2 建立水模型 此水模拟实验是根据相似原理进行。冷态模拟实验除了必须保证实验的几何条件相似之外，同时还必须 保证模型与实际研究现象的决定性准数相等[2] 。本实验遵循以下原则： 2.1 几何相似 RH 水模与实际设备尺寸比例的选择可以是任意的，考虑实验数据处理问题，实验选取相似比为 1/4， 即模型严格按照与原型 1/4 的比例缩小，保证几何相似。 8-600 第