微小异相去除夹杂物的实验研究.pdfVIP

1微小异相去除夹杂物的实验研究 倪 冰 刘 浏 (钢铁研究总院冶金工艺所，北京 100081) 摘 要 提出用脱氧净化剂产生细小气泡去除夹杂物和同时生成低熔点液态复合氧化物吸附夹杂物的控制技术，用 水模和 SiMo 电阻炉进行了冷态和热态实验。结果表明，脱氧净化剂在高温下分解生成小气泡和小渣滴，去除了细 -6 小夹杂物，处理后钢中的氧化物夹杂物显著降低，全氧最低达到 19×10 。 关键词 脱氧净化剂 气泡 复合氧化 物渣滴 夹杂物去除 Experiment Study on Inclusion Removal by Fine Heterophases Ni Bing Liu Liu (Central Iron and Steel Research Institute，Institute of Metallurgical Technology, Beijing, 100081) Abstract The inclusions in liquid steel were removed with fine dispersed heterophases induced by the deoxidizing purifyingagent in a SiMo furnace. The deoxidizing purifyingagent can produce both small bubble and low melting point compound deoxidation to attach the inclusions in the liquid steel. The results indicate that the number of oxide inclusions decreases to a lower level, and the total oxygen in the steel can approach to 19×10-6. Key words deoxidizing purifyingagentpurificant, bubble, compound deoxidation, slag drop, inclusion removal 去除去钢液中尽可能多的非金属夹杂物是炼钢操作的主要目的之一，采用小气泡去除夹杂物的研究已经 有许多报道[1~5] [6] ，笔者也曾对气泡去除夹杂物的过程和机理进行过研究 。除了小气泡外，复合脱氧可直接 产生低熔点、易聚合长大的液态复合氧化物，利用小液滴以渣洗的形式为夹杂物去除创造优良的初始条件[7] 。 综合两者的优点，通过向钢液中引入细小的异相颗粒——气泡和液滴，促进中的 Al O 夹杂与细小异相颗粒 2 3 的碰撞、聚集和长大，可以提高钢液的洁净度[8,9] 。本文利用水模实验和热态实验对细小异相去除夹杂物的 过程进行了研究。采用不同发泡剂含量的脱氧净化剂，净化剂在脱氧时产生细小异相，证实了捕获和去除夹 杂物的效果，为大生产中钢液的净化提供理论依据和实现手段。 1 水模实验 1.1 实验原理和方法 用水模型研究气泡去除夹杂物行为时，水力学原理应同时满足与粘性力有关的雷诺数和与重力和惯性力 有关的佛鲁德准数相似，即：Re水＝Re钢 ，Fr水＝Fr钢 。本实验借鉴某钢厂 100t 钢包为研究对象，用透明有机玻 璃制成模型，由于夹杂物粒子细小，欲得到清晰的图像，容器必须小一些。确定的几何相似比为 1:30，即 基金项目：中国钢研科技基金深题