炼钢过程引起的合金化热镀锌汽车外板表面缺陷解析.pdfVIP

炼钢过程引起的合金化热镀锌汽车外板表面缺陷解析1 1 1 2 1 杨 健 王睿之 职建军 祝 凯 （1. 上海市宝钢股份研究院冶金工艺研究所，上海 201900; 2. 宝钢股份炼钢厂，上海 201900 ） 摘 要 本文对于炼钢过程引起的合金化热镀锌（GA ）汽车外板表面缺陷的宏观、微观形貌进行了观察，对于有 镀锌层、去镀锌层和横截面上的夹渣或夹杂物的化学成分进行了详细的分析。炼钢过程引起的 GA 汽车外板表面缺 陷有保护渣、气泡和夹杂物三种缺陷，分别对于这三种缺陷的宏观、微观形貌和化学成分特征进行了研究，并探讨 了它们的形成机理。 关键词 炼钢 汽车外板 合金化热镀锌板 表面缺陷 Analyses of Surface Defects on the Hot Dip Galvanized Sheets for Car Body Panels Caused by Steelmaking Process 1 1 2 1 Yang Jian Wang Ruizhi Zhi Jianjun Zhu Kai (1. Metallurgical Process Department, Research Institute, Baosteel Co. LTD., Shanghai, 201900; 2. Steelmaking Plant, Baosteel Co. LTD., Shanghai, 201900) Abstract The macro- and micro-morphologies of the surface defects on the hot dip galvanized sheets for car body panels are observed. The composition analyses of the GA sheets with zinc coating, with zinc coating dissolved in hydrochloric acid, and on the cross-section surface of the sheets are conducted in this paper. There are three kinds of surface defects caused by steelmaking process, which are entrapment of mold powders and bubbles, and involvement of inclusions. The characteristics of the macro- and micro-morphologies, and the chemical compositions for three kinds of defects are carefully investigated, and their formation mechanisms are clarified. Key words steelmaking, car body panel, hot dip galvanized sheet, surface defect 1 前言 合金化热镀锌汽车外板（GA 外板）是一种对于表面质量要求很高的产品，随着中国汽车工业的高速发 展，近年来需求量急速增长。由于经合金化热镀锌工艺后，GA 外板表面由于炼钢引起的表面缺陷更加容易 显现，如何控制与减少由于炼钢工序的不当操作造成的 GA 外板表面缺陷成为亟待解决的重要课题。 GA外板表面缺陷包括：[1]炼钢类缺陷、热轧类缺陷、表面附着物类缺陷、冷轧加工变形类缺陷、机械 损伤类缺陷、腐蚀类缺陷等。其中炼钢工序引起的缺陷包括保护渣、气泡和夹杂物缺陷三类。由于炼钢类缺 陷产生的原因复杂，涉及铁水预处理、转炉吹炼、二次精炼、连铸等炼钢全工序过程，同时由于炼钢工