夹杂物对油井管钢氢致开裂的影响.pdfVIP

夹杂物对油井管钢氢致开裂的影响 艾芳芳 徐小连 陈义庆 钟 彬 李 琳 高 鹏 解德刚 （鞍钢股份有限公司技术中心，鞍山 114009 ） 摘 要 对油井管钢进行了pH 值为2.0 的浸泡溶液的HIC 试验。考察了油井管钢的抗HIC 性能，并着重分析了不 同种类夹杂物对钢板HIC 性能的影响，探讨了夹杂物作用的机理。研究结果表明：在强酸性腐蚀环境中，夹杂物 越多，钢对HIC 越敏感。诱发油井管钢氢致开裂的夹杂物主要为MnS 夹杂物、Al2O3 夹杂物和硅铝酸盐复合夹杂 物，其中长条状MnS 夹杂物危害最大。夹杂物诱发裂纹的初期形貌为夹杂周围出现空洞，空洞的扩展成为HIC 。 关键词 油井管 氢致裂纹 夹杂物 Influence of Inclusions on Hydrogen Induced Cracking of Oil Well Pipe Steel Ai Fangfang Xu Xiaolian Chen Yiqing Zhong Bin Li Lin Gao Peng Jie Degang （Technology Center of Angang Steel Co ．，Ltd ．，Anshan, 114009 ） Abstract HIC test in pH 2.0 corrosion solutions and inclusion analysis are carried out to oil well pipe steel. The mechanism of inclusion influence is discussed. The results indicate that HIC sensitivity of the sample with more inclusions is the biggest in strong acidic solution. The inclusions which induce HIC are MnS inclusion, Al2O3 inclusion and SiO -Al O inclusion, especially that strip-shaped MnS inclusion has greatest damage. Initial patter of HIC by inclusions is 2 2 3 cavity around inclusions, and then cavity develops HIC. Key words oil well pipe, HIC, inclusion 1 引言 油井管管材长期处于高硫化氢、二氧化碳和元素硫等含硫组分的环境中，并且环境中氯离子含量较高， 矿化度和含水率较高，所有这些因素及其交互作用的影响，使得油井管腐蚀严重，其中主要是硫化氢腐蚀， 破坏形式主要包括氢致开裂(Hydrogen Induced Cracking ，HIC)和硫化氢应力腐蚀(Sulfide Stress Corrosion Cracking，SSCC)和电化学腐蚀(Electrochemical Corrosion，EC)等，从而致使油井管失效。油井管的失效将 导致巨大的经济损失和严重后果，其安全可靠性和使用寿命对石油工业有重大影响。 影响 HIC 的因素很多，就材料本身而言，主要是钢的成分、组织以及夹杂物的数量和形状等因素。对 某一特定钢种来说，夹杂物的影响是最主要的。本文对油井管钢进行了HIC 试验，考察了油井管钢的抗HIC 性能，分析了不同种类夹杂物对钢板HIC 性能的影响，并探讨了夹杂物作用的机理。 第八届（2011 ）中国钢铁年会论文集 2 试验材料及方法 2.1 试验材料 试验材料是5 组不同成分的油井管钢，主要化学成分见表1。 表1 化