气体保护焊焊接工艺对ER50—6焊丝飞溅的影响研究.pdf

1气体保护焊焊接工艺对 ER50—6 焊丝飞溅的影响研究 肖九红 陈卫金 吴清明 袁 源 艾爱国 邱福祥 （湖南华菱湘潭钢铁集团有限公司，湘潭 411101 ） 摘 要 采用飞溅量化的方法，通过对不同钢厂的 ER50―6 焊丝在 CO2 气保焊、MAG 气保焊，以及不同焊接工 艺参数下飞溅的对比试验，来研究焊接工艺对气体保护焊焊丝飞溅的影响，证明了焊接工艺参数的选择和调整是影 响焊丝飞溅的非常重要的因素。同时，为降低气保焊飞溅问题提供了可靠的实验依据，并对气保焊焊接工艺设计及 其应用具有一定的指导作用。 关键词 气保焊 飞溅 焊接工艺 影响 Effect of GMAW on Welding Spatter of ER50-6 Wire Xiao Jiuhong Chen Weijin Wu Qingming Yuan Yuan Ai Aiguo Qiu Fuxiang (Hunan Valin Xiangsteel, Xiangtan, 411101) Abstract By spatter quantitative methods and through comparative tests of spatter for ER50-6 wire of different steel mills in the CO2 gas welding, MAG gas-welding and different welding parameter, the effect of welding process on spatter of gas shielded welding wire is studied, it is confirmed that the selection and adjustment of parameters for welding process is very important to influence spatter. Meanwhile, a reliable experimental basis is provided to reduce the gas-welding spatter, and it has a guiding role for the design and application of gas-welding process. Key words gas shielded welding, splash, welding, effect 1 引言 我国焊接材料用量逐年增加,尤其是气体保护焊丝用量大幅递增。随着我国焊接自动化技术推广应用和 焊接质量要求的不断提高，用户对气体保护焊丝提出了更高的要求。一些较重要的构件, 要求焊缝成形好、 飞溅小、低温冲击韧性高。焊接飞溅的大小是评定焊接材料工艺性能的一项重要指标。飞溅不仅污染环境及 工件,而且影响电弧的稳定性、降低熔敷效率, 还会堵塞喷嘴，造成送丝不畅，并增加焊工的劳动强度，为了 减少飞溅，国内外学者和技术人员进行了大量的研究工作，但通过飞溅的量化来研究焊接工艺对气体保护焊 焊丝飞溅的影响的较少。 针对这一情况，结合国内外有关资料，我们通过对不同钢厂的 ER50S―6 焊丝在 CO2 气保焊、MAG 气 保焊，以及不同焊接工艺参数下飞溅的对比试验，为降低气保焊飞溅问题提供了可靠的实验依据，并对气保 焊焊接工艺设计及其应用具有一定的指导作用。 2 飞溅产生机理 在 CO2 焊中，大部分焊丝的熔化金属可过渡到熔池，有一部分焊丝的熔化金属飞向熔池之外，飞到熔 肖九红，女，大本，高级工程师，从事材料研究工作。 气体保护焊焊接工艺对ER50—6 焊丝飞溅的影响研究 池之外的金属称为飞溅。 飞溅机理可从冶金因素角度和工艺因素角度分析：气体保护焊接时，熔滴和熔池中发生如下反应： 2CO =2CO+O ;FeO+C=Fe+CO;CO +Fe=FeO+CO 生成的 CO 气体在高温下急剧膨胀导致飞溅；工艺因素包括 2 2 2 设备的送丝速度、电流、电压等规范参数。由于焊接参数的不同，气体保护焊具有不同的