德标38Si7调质弹簧钢的开发.docVIP

?德标38Si7调质弹簧钢的开发 李绪宝,赵培田,吴玉峰 (莱芜钢铁集团有限公司特殊钢厂,山东 莱芜 271105) 摘　要：莱钢特殊钢厂采取50t UHP-EAF+50t LF 工艺生产德标38Si7调质弹簧钢,经严格冶炼及轧制,钢锭合格率达99.2%,成材率达92. 17%, 化学成分及机械性能均能满足德标DIN17221-72的要求。 关键词：38Si7调质弹簧钢;炉外精炼;冶炼;轧制 中图分类号：TF762+.5　　文献标识码：B　　文章编号：1004-4620(2000)02-000-03 Developing of 38Si7 Hardened and Tempered Spring Steel(DIN) LI Xu bao,ZHAO Pei tian,WU Yu feng (The Special Steel plant of Laiwu Iron Steel Group Co.,Ltd,Laiwu 2711 05,China) Abstract：The 38Si7 hardened and tempered spring steel (Deutsche Industrie Normen)was produced by 50t UHP-EAF+50t LF process in the special steel plant of Laiwu iron and steel group Co.,Ltd.Since strictly smelting and rolling process the percent of pass of ingot is up to 99.2% and finished products rate is up to 92.17%.Its chemical composition and mechanical properties can meet the requirements of DIN17221-72. Keywords：38Si7 hardened and tempered spring steel;ladle refining;smelting;rolling 1　　前言 　　德标38Si7调质弹簧钢是铁路上轨、枕弹条用钢,国内没有类似钢号,其工作条件十分恶劣,要承受多种形式的应力,并发生变形和破坏,因此38Si7要求必须具有较高的纯净度和均匀性,才能保证38Si7加工成的弹条具有高的弹性极限、屈服极限和疲劳极限,增加火车运行的稳定性。 　莱芜钢铁集团有限公司特殊钢厂(简称莱钢特殊钢厂)50t(UHP)-EAF+50tLF工艺可以满足38Si7的性能要求。通过炉外精炼和成份微调技术,把化学成分控制在较窄的范围内,最大限度地降低夹杂物的含量,细化晶粒组织,提高其淬透性和疲劳寿命。 2　　德标38Si7调质弹簧钢的主要技术条件 　　德标38Si7调质弹簧钢的生产成材及供货采用德标DIN17221-72标准,其主要性能(协议)要求如下: 　化学成分(熔炼分析)如表1所示。 表1　38Si7化学成分,% C Si Mn P S Cr Ni Cu 0.35～ 1.50～ 0.50～ ≤ ≤ ≤ ≤ ≤ 0.42 1.80 0.80 ≤ 0.045 0.045 0.35 0.35 0.20 　　(2)调质后机械性能见表2。 表2　38Si7机械性能 σs,MPa σb,MPa δ5,% ≥1030 ≥1180～1370 ≥6 　　(3)热轧状态下布氏硬度HB不大于302。 　晶粒度大于5级。 　钢材应有良好的表面质量,不允许有裂纹、折叠、飞边、气泡、夹杂、铁皮嵌入及表面脱碳等。 3　　试制工艺 3.1　　工艺流程 　　工艺技术条件见表3。工艺流程见图。 表3　工艺技术条件 电炉公称容量t 平均出钢量t 变压器容量MVA 出钢方式 LF钢包容量t 处理时间min 50 42±1 36/43.5 EBT 50 ±40 38Si7 工艺流程 3.2　　冶炼及铸锭工艺 　　(1)本钢种含〔Si〕量较高,具有吸气敏感性,而且要求钢质纯净,晶粒度大于5级,因此要求原材料必须清洁、干燥。炉料由切头及优质废钢组成;冶炼中充分脱氧、脱气、去除夹杂物。为了保证本钢种具有良好的机械性能,化学成分应控制在较窄的范围内,P、S含量应尽量低,见表4。 表4　化学成分控制目标　% C Si Mn P S Cr Ni Cu 0.37～ 1.60～ 0.60～ ≤ ≤ ≤ ≤ ≤ 0.40 1.70 0.70 0.030 0.030 0.25 0.25 0.20 　　(2)UHP电炉冶炼过程中注意熔化末期提前去P,造好泡沫渣防止钢水过氧化,快速升温,出钢温度165