冷轧低层错能面心立方金属形变机制的研究.docVIP

  Study on the micromechanism of f.c.c metals with low stacking fault energy during cold rolling: example of  5 10 15 20 alpha-brass# JIA Nan, ZHAO Xiang* (Key Laboratory for Anisotropy and Texture of Materials (MOE), Northeastern University, ShenYang 110819) Abstract: Micromechanism of α-brass which represents a face-centered-cubic (f.c.c.) alloy with low stacking fault energy (SFE) during cold rolling was investigated. Neutron diffraction, scanning electron microscope (SEM) and electron backscatter diffraction (EBSD) techniques were used to characterize lattice strain distributions and