高耐蚀Zn-Ni 合金电镀工艺.pdfVIP

11 1 Plating and Finishing Vo1．32 No．3 Serial No．204 文章编号：1001．3849(2010)03-0022—03 高耐蚀Zn·Ni合金电镀工艺 吴菊珍 (成都电子机械高等专科学校机电工程系，四川成都 610031) 摘要：介绍一种高耐蚀性Zn．Ni合金镀液配方及电镀工艺流程，阐述了zn-Ni合金镀液成分及工艺 条件的影响及维护方法。对zn．Nj合金镀层进行钝化处理后，通过中性盐雾试验，并与镀锌层进行 比较，zn—Ni合金镀层的耐蚀性高于镀锌层4～8倍。该配方具有成本低、工艺简单、分散性好、操作 方便及镀层易钝化等优点。 关 键 词：高耐蚀性；电镀；Zn．Ni合金；钝化 中图分类号：TQ153．2 文献标识码：A High Corrosion Resistant Zn-Ni Alloy Electr0plating Technology WU Ju—zhen (Mechanical and Electronic Engineering Department，Chengdu Electromechanical College，Chengdu 610031，China) Abstract：A sort of high corrosion resistant Zn-Ni alloy electroplating solution and the plating process flow were introduced．The maintaining method for the zinc—nickel plating bath was proposed．The contents of Zn Ni in the bath were determined by spectrophotometer．The corrosion resistance of the alloy coating was obviously increased with passivation treatment．This plating bath formulation had the virtues of low cost，process simple，good dispersivity，easy to operation and easy to passivation． Keywords：high corrosion resistance；electroplating；Zn—Ni alloy；passivation 而受到人们的欢迎，在汽车 、机械、钢铁及电子等 引 言 行业得到了广泛应用。 zn—Nj合金镀层的耐蚀性和耐磨性约为锌镀层 硫酸盐体系和氯化物体系的zn．Ni合金电镀工 的3～5倍，中性盐雾试验表明，该镀层出现白锈、红 艺，虽然阴极电流效率高，光亮度好，但合金镀层的 锈的时问均高于常用的锌镀层。Zn—Nj合金镀层在 成分受电流密度的影响比较大，稳定性较差，生产应 较高温度下的耐蚀性优于纯锌镀层，耐热高达200～ 用受到一定的限制。本工艺为无氰锌酸盐镀液 250℃，可焊性和延展性与锌相当，与油漆的结合力 zn．Ni合金电镀工艺，经分析 镀层中W(Ni)为 良好，氢脆几乎无，适合于要求耐疲劳如弹簧、紧固 10％-15％，操作方便，溶液稳定，防腐性能优越。近 件和其它结构件电镀…，能在较高温度下使用，因