300MW机组电液伺服阀材料的失效分析与表征.pdfVIP

300MW 机组电液伺服阀材料的失效分析与表征 300MW 机组电液伺服阀材料的失效分析与表征 郑慰慰 指导老师 杨振国 (复旦大学材料系 200433) 摘要 电液伺服阀是数字电液控制系统的关键部件, 其工作状况直接会影响汽轮发电机组的 安全可靠性 本文通过对上海某电厂电液伺服阀的重大失效案例分析 对伺服阀的失效起因 材料劣化状况 抗燃油介质以及清洁剂性能进行了详细的表征与剖析 结果发现腐蚀介质和 抗燃油的污染引起电液伺服阀的腐蚀和磨损的交互损伤 并提出了相应的防范措施和改进建 议 关键词 电液伺服阀 失效分析 腐蚀与磨损 抗燃油 Abstract: Electro-hydraulic servo valve, which directly influences the reliability of steam turbine-generator unit, is a key component of digital electro-hydraulic control system. By virtue of a thorough analysis for serious failure case of electro-hydraulic servo valve occurred in a power plant of Shanghai, the failure source, material quality, flame resistant oil and detergent characteristic of electro-hydraulic servo valve were systematically characterized and assessed. It is shown from analysis results that the corrosive medium and pollution of flame resistant oil result in failure of the servo valve which is caused by interaction damage of corrosion and wear; and thus the corresponding improvement and suggestion are put forward. Keywords: electro-hydraulic servo valve failure analysis corrosion and wear flame resistant oil. 1. 引言 随着数字电子技术和高液压技术的发展, 目前 300MW 以上机组的汽轮机调节保安系 统均采用了数字电液调节系统(Digital Electro-hydraulic Control, DEH), 从而提高了汽轮机运 行的安全性 可靠性和经济性 电液伺服阀是机组DEH 系统的关键部件 其工作可靠性将 直接影响到机组的安全稳定运行[1] 下图示意的是一种喷嘴型 MOOG 电液伺服阀剖面结构 它的节流和增压工作原理主要 是力矩马达作为电液转换装置 将电信号转换为转子的角位移 再以喷嘴挡板作前置放大把 角位移转为较弱的液压控制油流 最后再利用液压功率放大级转换较大的液压功率输出油 流 由于阀芯和阀套凸型工作面间隙极其微小 通常是以微米级计量 任何元件尺寸哪怕发 生极其微量的变化 都会导致 MOOG 阀泄漏失效 从而引起整个 DEH 系统的失效甚至瘫 痪 图 1 MOOG 阀阀芯阀套剖面示意图 因此 近几年来 在役电液伺服阀运行的安全可靠性受到了人们的广泛关注并对运行 中出现的各种失效案例进行了比较详细地分析和研究[2-6] 较多地论述了系统油液污染对伺 178 复旦大学 政学者论文集 2002 服阀工作可靠性的影响 着重于对系统油液中所含杂质 具有磨料特点 伺服阀对这些污染 杂质抗磨损机理及