《化学通报》在线预览版 共沉淀法制备 α-磷酸三钙 杨洪 傅山岗 （河南师范大学生命科学学院，河南新乡 453007） 摘 要 以NHHCO 、(NH ) HPO 和Ca(NO ) ﹒4HO为原料，由液相共沉淀法制得分子比2:1的CaHPO 和CaCO 混合粉体，经高 4 3 4 2 4 3 2 2 4 3 温煅烧处理后制得 α-磷酸三钙（α-TCP）粉末。用化学分析法分析了混合粉体的钙磷比，X 射线及透射电镜(TEM)分析了 α-磷酸三钙粉末的晶相组成、微观形貌。结果表明，共沉淀的方法可以得到 α-磷酸三钙；与机械混合法相比，共沉淀法 制备的粉料在高温下有较快的α-磷酸三钙转化速率。 关键词 共沉淀 α-磷酸三钙 粉体 Preparation of α-Tricalcium Phosphate by Co-precipitation Yang Hong Fu Shan-gang (College of Life Sciences，Henan Normal University. Henan Xinxiang 453007) Abstract CaHPO and CaCO mixture powder were synthesized from the NH HCO ，(NH ) HPO and Ca(NO ) ·4H O by 3 3 4 3 4 2 4 3 2 2 coprecipitating way. The mixed powder was calcined at high temperature, and to obtain α-tricalcium phosphate(α-TCP). Ca/P molecular ratio of the mixed powder was determined with chemical analysis method. The crystallite phase, micro-morphology and crystallite size of α-TCP powder were characterized by XRD and TEM . The results showed that α-TCP could be prepared with co-precipatited method, and obtained powder have more fast change rate towards α-TCP phase at high temperature 。 Keywords coprecipitation, α-tricalcium phosphate(α-TCP), Powder 由于磷酸盐骨水泥(CPC) 具有良好的生物相容性和生物活性、植入人体后反应温和、基本不放热,而且 在手术过程中能根据缺损部位随意塑型等优点,近年来引起了各国研究者的广泛关注[1～5] 。人们相继研制了 一系列磷酸钙骨水泥产品以适应不同部位人体硬组织修复的需要。 所制备的骨水泥根据水化产物不同大致分为两类[6] ：羟基磷灰石类 （HA ）和二水合磷酸氢钙 （DCPD ）。 制备HA类骨水泥的主要原料为磷酸四钙(TTCP, tetracalcium phosphate, ,Ca (PO ) O)、α-磷酸三钙（α-TCP，