有机添加剂对黏结砂浆性能的影响.pdfVIP

1 文章编号：1007—046X(2011)02—0035—03 孽态建材 有机添加剂对黏结砂浆性能的影响 Influence of Organic Additive on Bonding Mortar Performance 刘文斌，鞠宇飞 (常州工程职业技术学院，江苏 常州 213164) 摘 要：研究可再分散胶粉、纤维素醚、淀粉醚、SM高效减水剂对黏结砂浆性能的影响。结果表明：可再分散胶粉、纤维素 醚并非越多越好，实验中掺量为15％o和3‰时砂浆性能最优。纤维素醚掺量从O‰～10％，砂浆的舍气量从3．60％--40％。 淀粉醚的掺入对纤维素醚并没有起到协同效应，SM高效减水荆和纤维素醚相互影响，掺入后砂浆减水效果不佳，性能 出现下降。 关键词：黏结砂浆；胶粉；纤维素醚；淀粉醚；SM 高效减水剂 中图分类号：TU57 8．1 文献标识码：A Abstract：Influences of re—dispersible powder，cellulose ether，amylum ether，SM super—plasticizer on bonding mortar performance were studied．The result indicates the bonding mortar performance don’t improve with increase of quantity of re—dispersible powder and cellulose ether．When their contents are 1 5％oand 3 1 5％o，the mortar performance is optimized．When the content of cellulose ether is form 015％0 to 1015％。．the air content is form 3．6％to 40％．Adding amylum ether doesn’t cooperate with cellulose ether．The mortar performance descends through adding SM super—plasticizer，the reason is possibly passive influence between SM super-plasticizer and cellulose ether． Key words：bonding mortar，re—dispersible powder,cellulose ether,amylum ether，SM super-plasticizer 0前言 (3)外加剂。可再分散乳胶粉(国产，主要成分为醋酸 乙烯脂一乙烯)；纤维素醚(国产，黏度l0万mPas)；淀 黏结砂浆是以水泥、石英砂、聚合物胶结料配以多种 粉醚(国产)；SM高效减水剂。 添加剂经混合而成，具有优良的柔韧性和黏结性能，以及 1．2实验方法 良好的抗下垂性、保水性、耐水性。本文主要是通过对胶 粉、纤维素醚、淀粉醚、SM减水剂的研究，分析他们在 黏结砂浆实验过程按JGJ 70—1990《建筑砂浆基本性 水泥中的作用，及他们之间的协同效应。 能试验方法》的规定，在标准养护条件下分别养护7 d 和28 d测试其性能。 1实验材料及方法 2实验分析 1