香草醛改性壳聚糖的制备及其吸附能效.pdfVIP

中国环境科学 2000,20(1) 6164 China Environmental Science 香草醛改性壳聚糖的制备及其吸附性能 邵 健,杨宇民 南通医学院化学教研室,江苏 南通 226001 摘要 香草醛经Schiff 反应对壳聚糖进行了修饰.研究了产物对 Cu2+ Pb2+ Cd2+ Zn2+ 的吸附性能,同时考察了pH 值 时间 温度等因 素对吸附的影响.结果表明,改性后的壳聚糖具有不流失, 易再生的特点,且对金属离子的饱和吸附量比壳聚糖的大(改性后的壳聚糖对Cu2+ Pb2+ Cd2+ Zn2+ 的饱和吸附量分别为143.5 585.9 357.7 178.4mg/g). 关键词 壳聚糖 香草醛 吸附 制备 中图分类号 X131 文献标识码 A 文章编号2000 Chitosan modified by vanillin and its adsorption property. SHAO Jian, YANG Yu-min (Department of Chemis- try,Nantong Medical College, Nantong 226001,China). China Environmental Science. 2000,20( 1) 6164 Abstract Chitosan was modified by vanillin via Schiff s reaction and the resulting product was investigated in relation to 2+ 2+ 2+ 2+ its adsorption behavior for metal ions such as Cu ,Pb ,Cd and Zn as well as the effects of pH, time and temperature on the adsorption behavior. The results indicate that the modified chitosan has higher adsorption capacities than the unmodi- 2+ 2+ 2+ 2+ fied one (the formers adsorption capacities for Cu ,Pb ,Cd and Zn are 143.5,585.9,357.7 and 178.4mg/g) and has good kinetic properties-uneasily running off and being regenerated easily. Key words chitosan vanillin adsorption preparation 天然高分子材料壳聚糖(CTS)作为金属离子 1.2.1壳聚糖微粒的制备 将壳聚糖溶解在 [1] 的吸附剂已有报道 , 但在 pH 值较低的情况下 2%HAc 溶液中,得浓度为5%(W/W) 的黏稠溶液. 使用壳聚糖时,会因其溶于水而造成吸附剂的流 在搅拌下向此溶液中滴加1mol/L 的NaOH 溶液 [2] 失,不利于再生 . 也有人报道了对壳聚糖进行交 至pH 值为 89,得絮状壳聚糖的沉淀.将此体系 联,虽然交联壳聚糖的流失情况得到改善,但却大 用高速组织捣碎机以 12000r/min 匀浆 6min,得 [3] 大降低了金属离子的饱和吸附量 .本课题选用 弥散的近似于乳状的悬浊液.离心,水洗沉淀至中 香草醛(4- 羟基-3- 甲氧基苯甲醛)对壳聚糖进行 性,抽滤.少量无水乙醇洗 3 次(取少量在红外线 了修饰,并对修饰物 V-CTS(Na) 的吸附性能进行 快速干燥器中烘干,研磨粉碎). 了测试.结果表明,香草醛改性的壳聚糖与壳聚糖 1.2.2香草醛修饰的壳聚糖吸附剂的制备 将 相比, 前者对金属离子的饱和吸附量大,具有在酸