11Cr17钢零件过盈配合的数值模拟及断裂原因分析.docVIP

11Cr17钢零件断裂分析 212003） 摘要:对11Cr17钢制杠杆传动器零件的冷压过盈装配过程中扇形块断裂的原因以及断裂方式进行了分析研究。采用对扇形块断裂件的断口形貌、金相组织进行了检测分析。结果表明，该零件为脆性断裂，断裂件顶部圆弧处的外侧表面存在着加工缺陷，孔的边缘表面上也有装配时机械损伤痕迹，零件内部存在着夹杂物，这些缺陷的出现降低了材料的强度，是诱发裂纹、导致零件脆性断裂的重要原因。 Fracture Failure Analysis of 11Cr17 Steel Lever Actuator Dai Anlun, Niu Wenming, Zhu Zhiyuan (School of Materials Science and Engineering, Jiangsu University of Science and Technology, Zhenjiang 212003, China) Abstract: The fracture reason and model of 11Cr17 steel lever actuator’s fan-shaped part in the cold press interference assembly process were analyzed. The microstructures and fracture morphologies of the failure part were studied by optical microscope, scanning electron microscope and energy dispersion spectrum analyzer. The results show that the fan-shaped part was broken by brittleness, there are some processing defects which exist on the top of circular arc’s outer side surface, some assembly mechanical damages exist at the edge of hole’s surface and some inclusions also exist at the center of fracture. These defects reduce the strength of part, are the important causes which induces crack and brittle fracture of the fan-shaped part. Key words: fracture morphology; brittle fracture; processing defects; inclusions 引言 某公司用11Cr17钢11Cr17钢是一种马氏体不锈钢，它在所有不锈钢、耐热钢中，硬度最高 1.检验内容和方法 1.1 检验材料 检验所用零件材料为11Cr17钢，其成分如表1所示。 扇形块零件加工工序为：棒材－热模锻成型－机加工－热处理（淬火＋低温回火）－精加工－过盈配合装配，其中淬火采用液氮冷却，即气淬。试样热处理后的性能及其参数见表2。表1 11Cr17的化学成分（%） Table 1 Chemical composition of 11Cr17 alloy 成分 C Si Mn S P Cr Ni Mo Fe 含量 0.95~ 1.20 ≤1.00 ≤1.00 ≤0.30 ≤0.035 16.00~18.00 ≤0.60 ≤0.75 余量 表2 试样的性能参数 Table 材料 屈服强度 （MPa） 抗拉强度 （MPa） 伸长率 （%） 弹性模量 (Pa) 泊松比 11Cr17 1400 1650 1.5 2.07E5 0.3 0.2 1.2 断口检验 在对失效扇形零件断口进行宏观检查的基础上，于断口重点部位用电火花线切割切取样，经汽油清洗，再用丙酮溶液超声波清洗、烘干用日本电子公司JSM-7001F场发射扫描电镜对该断裂断口进行微观分析。 另切取样品，经镶嵌保护后磨、抛光成金相样，用德国LEICA公司DM2500型光学显微镜及日本电子公司JSM-7001F场发射扫描电镜分析其金相组织，然后用HRS-150型数显洛氏硬度计测其硬度。断裂件断口形貌分析 .1断裂件断口的宏观形貌分析 图可[1]。 图 断裂件宏观形貌及断口）断裂处局部）断口图零件的断口宏观形貌，可见在断口的左上侧表面