高质量轴承钢金相夹杂物的控制研究 ·1 · 高质量轴承钢金相夹杂物的控制研究 1 1 2 李 涛 王海江 吉海峰 （1.东北特钢集团技术中心抚顺分中心，抚顺 113000 ； 2. 东北特钢集团抚顺基地企管部，抚顺 113000 ） 摘 要 本论文叙述了钢中各类型金相夹杂物对轴承寿命的影响以及高质量轴承钢对金相夹杂物的要求。并以生产 实践为依据，着重分析了影响各类型夹杂物生成的主要因素，提出了具体控制方法。 关键词 高质量轴承钢 金相夹杂物 控制研究 The Study of Controlling Metallographic Inclusion of High-quality Bearing Steel Li Tao1 Wang Haijiang1 Ji Haifeng2 (1. Fushun Branch of Technology Center of Dongbei Special Steel Group, Fushun, 113000; 2. Department of Enterprise Management of Fushun Base of Dongbei Special Steel Group, Fushun, 113000) Abstract In this paper, the effects of metallographic inclusion on life of bearing and the requirement of high-quality bearing steel to metallographic inclusion are described. Moreover on the base of production practices the main factors of influencing different type of inclusion formation are emphasized to analyse and detailed controlling means are put forward. Key words high-quality bearing steel, metallographic inclusion, study of controlling 轴承钢中的非金属夹杂物，破坏了金属的连续性，在轴承工作过程中所产生的交变应力的作用下，易于 引起应力集中，成为疲劳裂纹源，降低轴承的疲劳寿命[1] 。因此，减少钢中的夹杂物含量是提高轴承疲劳寿 命的主要途径。对于高质量轴承钢既要要求低的夹杂物总量，同时又要要求夹杂物以细小、均匀、弥散的塑 性夹杂物分布[2,3] 。因此，我们在冶炼过程中要尽量按照以上两条原则来控制夹杂物，以达到高档轴承钢性 能的要求。 1 高质量轴承钢对金相夹杂物的要求 国内一般轴承钢对高倍夹杂物的要求主要是根据GB/ T18254 条件执行，而低钛轴承钢对高倍夹杂物的 要求则更为严格，如SKFD33-1B10001SKF3 热轧棒材技术条件中的规定如表 1 所示，标准要求高倍夹杂应 该对6 个金相试样进行评级，所有6 个试样的平均级别应该不大于表1 中规定的级别，同时所有夹杂物类至 少4 个试样的级别不大于表1 中规定级别；国外某大型轴承制造公司在中国国内订货时的技术协议规定如表 2 所示，标准要求高倍夹杂应该对6 个金相试样进行评级，所有6 个试样的夹杂物级别应该不大于表2 中规 定的级别。 ·2 · 第九届中国钢铁年会论文集 表 1 SKF 标准规定的高倍夹杂物级别 A 类