镁合金表面直接化学镀镍研究.pdfVIP

第八届2l省4市铸造学术会议论文 镁合金表面直接化学镀镍研究 苏绍玉陈晓谢华何晓峰 (福州大学机械工程学院，福州350002) 摘要：为了提高镁合金的耐蚀性，对表面进行了化学镀镍。研究了硫脲、pH值、温度及时间对化学镀层 及镀速的影响，测定了镀层的显微硬度、结合力和耐蚀性。显微硬度结果表明镀层具有较高的耐蚀性和硬 度：锉磨实验表明镀层具有较好结合力：极化曲线表明化学镀后试样耐蚀性大大提高；X射线衍射表明镀 态镀层为非晶态，热处理能使镀层晶化，当热处理温度达到400℃时，晶化效果尤为明显。 关键词：镁合金化学镀镍镀层耐蚀性 on ofElectrolessNi on StudyTechnology Plating MagnesiumAlloys SU Shaoyu，CHENXiao，XieHua，HEXiaofeng ofMechnical ofFuzhou (Department EngineeringUniversity，Fuzhou350002) to Abstract：EleetrolessNi on isresearched itscorrosion platingmagnesiumalloy improve andtimetotheinfluenceofclad and includingSulfourea．pH．temperature layer speed andanti--corrosionofthe aremeasured．Multinomial imerohardness，adhesionstrength platinglayer resultsallshowthatthe have hardnessandanti--corrosion adhesive platinglayers higher capability．Excellent forceofthe havebeenobtained indicatesthe are diffractometry layers platinglayers too．X—ray plating inthe ofheattreatment．、vhenthe comesto crystallization amorpho啦states．but happensprocess temperatureup effectsaremoreobvious． 400℃．crystallization words： ElectrolessNi Anti--corrosion Key Magnesiumalloys platingPlatinglayer O前言 镁是工程材料中相对密度最小的金属元素，约为1．749／cm3；镁合金则是实际应用中最轻的金属结构材 料。纯的金属镁作为结构材料应用很少，但镁与其它金属组成的合金是一种很好的轻质结构材料，其重量 约为钢的l／5，锌的1／4，铝的2乃。