硫铝酸盐水泥基自流平灌浆料研究.pdfVIP

硫铝酸盐水泥基自流平灌浆料研究 杜纪锋 叶正茂 芦令超 常钧 （济南大学济南 250022 ） 摘要 本文研究了高效减水剂、缓凝剂及矿物掺合料对硫铝酸盐水泥的影响，结合扩展度、抗折强度、抗压 强度等指标确定试验配比，制备水泥基灌浆材料。研究表明，该灌浆水泥初始扩展度可达到275 mm，凝结 时间可调，硬化浆体结石强度高，12 h抗压强度可达48 MPa，3 d强度达到55 MPa。28d膨胀值为7.8×10-4 ， 属微膨胀。通过SEM、EDS等方法对灌浆料水化产物进行微观结构分析表明，12 h内即生成了大量钙矾石晶 体,水泥石迅速产生强度,随着水化反应的进行,钙矾石晶体不断地生长、长大，并有大量的钙矾石继续生成， 产生体积膨胀，宏观表现为较高的早期强度和体积膨胀性。 关键词 硫铝酸盐水泥 灌浆料 力学性能 膨胀干缩 Study on the sulphoaluminate cement based self-leveling grouts DU Ji-feng, YE Zheng-mao, LU Ling-chao，CHANG Jun (School of material science and Engineering, University of Jinan, Jinan 250022, China) Abstract: In this paper the factors affecting the mix proportion of the self-leveling grouts were investigated including the quantity of sulphoaluminate cement ,sand, water reduer and retarder. The results show that the initial Flowing diameter is 275 mm; the compressive strength of the grouts is 48MPa, 55MPa at 12h and 3d curing ages, that exhibits the good performance of the strength; The expansion ratio is 7.8×10-4 ，in 28d standard curing.The microstructue of the grouts were tested by means of XRD-EDS, a lot of gel and columnar ettringite hydrates are produced in initial 12h. So the grouting material have higher early strength. Key words: sulphoaluminate cement; grouting material; Mechanical Properties; Expansion and Shrinkage 中图分类号：TQ 172 文献标识码：A 0 前言 优良的性能。由于硫铝酸盐水泥具有快硬、 长期以来，灌浆料在建筑工程中是一类 早强、微膨胀、高流动性及适宜可操作时间 应用量大，使用面广的建筑材料。特别是自 等特点，可以用来开发研制自流平灌浆料。 流平材料，先后开发了石膏系、水泥系及聚 1 实验原料 合物水泥自流平砂浆,普遍应用于机械设备 实验所用的主要原料：水泥硫铝酸盐水 安装和加固修补工程中[1-2] 。目前在使用水 泥，淄博生产, 比表面积为450 m2/kg ；磨细 泥基灌浆料时, 由于普通水泥体积收缩容易 矿渣（slag ），济钢产；Ⅰ级粉煤灰(FA)，邹 产生微裂纹，导致支座安装后造成支座板下 城电厂产；砂，标准砂（ISO ）；济南产；高 不密贴，另外,强度发展慢，而且耐久性