镁合金在大变形和高应变率下塑性变形与研究进展_宁俊生.pdfVIP

　 67 Research and Progress of Plastic Deformation of Magnesium Alloys at High Strain Rate and Large Deformation 1 2 1 , , (1 , 264005; 2 , 264000) 1 2 1 I G Jun-sheng , FA Ya-fu , PE G Xiu-feng (1Physics Department of Yantai University, Yantai 264005, Shandong, China; 2 Yantai Branch of o.52 Institute of China Ordnance Industries Group, Yantai 264000, Shandong, China) :。 , 、。 , 。 :;;; :TG146.22　　:A 　　:1001-4381(2007)09-0067-07 Abstract:Study about micro-structural changes of magnesium alloys under large strains and severe plastic deformation were introduced.Attention is concentrated on the research about the plastic de- formation of magnesium alloys under impact loading and high strain rate.Meanwhile, the properties and physical mechanisms of plastic deformation of magnesium alloys under different loads and over a wide range of temperatures were reviewed.Finally, several formula for describing the behaviors of magnesium alloys under dynamic loading at high strain rate was summarized briefly, and some sugges- tions on the study of magnesium alloys used as structural materials were offered. Key words:magnesium alloy;large plastic deformation;high strain rate;impact loading 　　, 200MPa, σb240～280MPa, ; 。、 Mg-Al-Zn , , , b 0 .2 。