复合掺杂对贫铁配方的MnZn功率铁氧体材料电、磁性能的影响.pdf

复合掺杂对贫铁配方的MnZn 功率铁氧体材料的电、磁性能的影响 Abstract MnZn ferrite is one of the basic materials of modern electronic and information industry. With the rapid development of telecommunication, electronic and computer technology, low power loss ferrite is needed for application at high frequency. In this thesis recent development of MnZn power ferrites are reviewed first. The crystal structure, magnetic origin and the procedure of solid phase reaction of the MnZn ferrite have then been introduced. Finally, the methods of lowering power loss and some magnetic parameters of MnZn power ferrites have been discussed. The effects of Fe-poor composition, SnO2 and ZrO2 co-doping and sintering temperature on electrical and magnetic properties of MnZn ferrites prepared by the classic oxide ceramic procedure are investigated. Ferrites with Fe-poor composition show high resistivity and low eddy current loss. This is believed to result from the fact that the Fe-poor composition reduces the content of Fe so the 2+ 3+ transition between Fe and Fe decreases. The resistivity of the ferrite with 48mol% Fe O is 2 3 19.3Ω•m. Proper SnO2 and ZrO2 co-doping decreases the magnetic loss of the MnZn ferrite. There are 4+ several reasons. Zr ions are enriched at the grain boundaries where forms an insulator layer with 4+ high resistance so the resistance of the ferrite increases and the eddy current los