La—Mo阴极发射性能及机理研究.pdfVIP

维普资讯 · 研 究 与 设 计 · La—Mo阴极发射性能及机理研究 王金淑 ，李保真 ，周美玲 (1．北京工业大学 材料学院，北京 100022；2．京东方科技集团有限公司，北京 100016) A StudyoftheEmissionPropertyandM echanism ofLa-M oCathode WANG Jin-shu ，LIBao—zhen ，ZHOU Mei—ling (1．SchoolofMaterialsScienceandEngineering，BeijingPolytechnicUniversity，Beijing100022，China； 2．BOETechnologyGroupCo．Ltd，Beijing 100016，China) Abstract：TheemissionpropertyofLa—M ocommercialtubeandtheemissionmechanism ofthiskindof cathodehavebeenstudied．Thevalenceofelementlanthanum ofcathodematerialhasbeenstudiedbyU— sing thermodynamiccalculation，in-situhightemperatureX—rayphotoelectron spectrum．On thebasisof experimentresults．theemissionmechanism ofLa—M ocathodehasbeen discussed．Experimentalresults show thatthesaturatedpulseemissioncurrentofLa—MoFU6051electronictubeiSabout2．32timeshigher thanthatofTh—W tube．andtheheatingpowerisonly47 ofTh—W tube．Ithasbeenprovedthatmolyb— denum carbidecanreducelanthanum oxidetometalliclanthanum．Itisshownthatitistheformationofa monatomiclayerofmetalliclanthanum atthesurfaceofafilamentthatiSthecauseoftheemissivityofthe cathodesincethemonatomicactivesurfacelayerhasalowerworkfunctionthancleanmolybdenum． Keywords：La—Mothermioniccathode；Emissionproperty；Emissionmechanism 摘要：研究了实用型 Ira—Mo电子管的发射性能，并采用热力学计算、原位 XPS等方法对 LaMo阴极中La的价态进行了 研究，探讨 了该阴极的发射机理 。实验结果表 明，实用型 FU6051La—Mo电子管的阴极饱和脉冲 电流密度为 同型号钍钨管的 2．32倍 ，而所需加热功率仅为钍钨 阴极的47 。高温下 I．aO。可以被 MoC还原成单质 La。在阴极工作过程 中，还原得到 的La覆盖在 Mo基体表面 ，降低 了基体 Mo的逸 出功，促进 了阴极的发射 。 关键字 ：La—Mo；热 阴极 ；发射性能 ；发射机理 中图分类号 ：0462 文献标识码 ：A 文章编号 ：1002—8935(2007)06—0005—03 ThO一W (简称 Th—w)阴极是 目前 电子管 中广 阴极在内的原子膜阴极发射机理一直未得到实验证 泛使用的阴极 ，众所周知 ，该种 阴极具有严重 的放射 实。文献 [5]认为 ，稀土氧化物 (Sm O。，Eu0。和 性污染，急需研制新型 阴极来取代 。LaO。一Mo(简 YbO。除外)化学稳定性很好 ，LaO。不能被 MoC 称 L