X100直缝埋弧焊管焊接残余应力测试分析.docVIP

X100直缝埋弧焊管焊接残余应力测试分析 摘 要：X100直缝埋弧焊管属于管道钢的新技术产品，通过研究其残余应力，从而可以提高其使用效率及寿命，使管道建设降低成本和损失，获得更好的经济效益。 文中采用了盲孔法进行对X100直缝埋弧焊管焊接残余应力的测试分析，通过对实验数据及其平面图形的分析，从而了解其焊缝接头周围的轴向残余应力和周向残余应力的数值及分布情况，判断其分布规律。通过实验分析，得知X100直缝埋弧焊管的内表面及其外表面的焊缝接头周围的轴向残余应力和周向残余应力的峰值，并通过分析得出其分布曲线，明了其分布规律。 关键词：残余应力；盲孔法；轴向；周向 The X100 straight seam submerged arc welded pipe welding residual stress test analysis Abstract:X100 LSAW belonging to new technology products of steel pipes.Through the study of residual stresses,could improve its efficiency and lifetime,make pipeline construction to reduce costs and losses,obtain better economic.This paper uses a blind hole method for X100 LSAW pipe welding residual stress test analysis,Of experimental data and analysis of shapes,To understand the weld joints around the axial and circumferential residual stress value and the residual stress distribution,to determine its distribution.Through experimental analysis,Learning X100LSAW pipeinner surfaceandan outer surfaceof theweld jointaround theaxial residualstressand circumferentialresidual stresspeak,By analyzing theresultsof itsdistribution curve,acknowledges itsdistribution. Key words: Residual stress;Blind - Hole Method; Axial ;Circumferential 目 录 1 绪论 1 1.1 研究背景及意义 1 1.2 X100直缝埋弧焊管 2 1.2.1 高钢级管线钢发展应用概况 2 1.2.2 X100级管线钢力学性能 3 1.2.3 X100直缝埋弧焊管焊接工艺 4 1.2.4 X100管线钢的焊接 4 1.2.5 X100级管线钢相关技术问题 5 2 焊接残余应力简介 7 2.1 焊接残余应力概述 7 2.2 焊接残余应力的产生原因 7 2.3 残余应力的影响 9 2.4 消除残余应力的方法 10 2.5 残余应力的测量方法 11 2.5.1 传统的残余应力测量方法 11 2.5.2 新型的残余应力测量方法 13 2.5.3 残余应力测量的 14 3 残余应力测试实验 16 3.1 实验方案 16 3.2 盲孔法测定残余应力 18 3.2.1 实验装置及材料 18 3.2.2 盲孔法测残余应力的原理 18 4 实验数据整理及结果分析 22 4.1 实验数据整理 22 4.2 实验结果分析 22 3.3 实验误差分析 25 5 总结 26 参考文献 27 致 谢 28 1 绪论 1.1 研究背景及意义 随着天然气的需求在全球范围内持续增长, 天然气供应以及现有输送系统使得天然气市场呈现供不应求的现状, 如何实现经济有效的天然气长距离输送已成为现今全球经济大环境中的重要一环。为了提高其输送效率、降低铺设管线费用, 高钢级管线钢将成为今后长距离输气管线铺设的主要用钢。 残余应力水平是焊管质量的重要指标较高的残余应力会导致管线工作能力严重下降高值拉伸残余应力会削弱其承压能力应力集中处易产生应力腐蚀,成为管线安全的重大隐患。影响油气管线的使用安全，其对结构刚度、受压杆件的稳定性、静载强度、疲惫强度、焊件加工精度和尺寸稳定性均有影响。因此对焊管中残