N、Zn共掺杂纳米TiO光催化剂的制备及其光催化降解甲基橙应用研究.docVIP

N、Zn共掺杂纳米TiO2光催化剂的制备及其光催化降解甲基橙应用研究 摘要： 以tioso4和znso4·7h2o为原料，nh3·h2o为沉淀剂，采用超声波-微波化学共沉淀法制备具有可见光催化活性的n、zn共掺杂纳米tio2纳米粉体，并用xrd、uv-vis对其进行了表征。在可见光下，考察了n、zn共掺杂纳米tio2光催化降解甲基橙的光催化性能。通过正交试验得出降解甲基橙的最佳工艺条件，并在最佳条件下做验证实验得出在太阳光下照射6h，光催化剂重复使用4次后降解率仍可到达74.2%，有超声分散、搅拌的条件下降解甲基橙降解率达到98.2%。 abstract: n、zn co-doped tio2 nanometer photo-catalysts（nzt）, which have photo-catalysis in invisible spectral rang, were prepared with tioso4 and znso4·7h2o as raw materials, nh3·h2o as precipitant by co-precipitation method. it was characterized by xrd and uv-vis. photo-catalytic activities of n、zn co-doped tio2 catalysts under visible light irradiation by photo-degradation of methyl orange. verification experiment in the optimum conditions showed that the degradation ratio of methyl reached 98.2%, under sunshine for 6h, with ultrasound dispersing and whipping, and it’s still 74.2% four times reused. 关键词： tioso4和znso4·7h2o；纳米粉体；光催化剂 key words: tioso4 and znso4·7h2o；nanometer；photo-catalyst 中图分类号：th6 文献标识码：a 文章编号：1006-4311（2012）11-0309-02 0 引言 印染废水种类多、水量大、含有机物成分复杂、可生化降解性差，其中含有的有毒成分可以削弱有机污染物的微生物矿化作用，会引起水生生态系统微生物的减少；导致水体生态系统的破坏其中属于偶氮染料的甲基橙是具有代表讯的一种，废水中残留的染料组分排入水体会造成水体透光率下降，它易溶于水，其性质十分稳定，用传统的生物降解方法难易降解。tio2光催化技术能使有机污染物完全氧化分解去除，它通过生成具有强氧化势的·oh自由基，另外，光催化技术具备可利用太阳能、不产生二次污染，成为最具潜力的染料废水处理方法之一。随着技术的发展，它还具备使用设备简单、操作条件容易控制等优点，被业界广泛应用。 通过正交试验，可得出降解甲基橙的最佳工艺条件，以期为难降解印染废水的可见光催化处理提供依据。本文以tioso4和znso4·7h2o为原料，nh3·h2o为沉淀剂，采用超声波-微波化学共沉淀法制备具有可见光催化活性的n、zn共掺杂纳米tio2纳米粉体（简称nzt），并用xrd、uv-vis对其进行了表征。在可见光下，考察了n、zn共掺杂纳米tio2光催化降解甲基橙的光催化性能。 1 实验部分 1.1 试剂与仪器 试剂：所用试剂均为分析纯，购自天津市化学试剂三厂。 仪器：x射线粉末衍射仪，日本岛津公司xrd-6000；测uv-755b型紫外-可见分光光度计，上海楚定分析仪器有限公司。 1.2 催化剂制备 按zno与tio2的比例，量取一定质量的硫酸锌和硫酸氧钛，分别溶解，混合均匀后，置于恒温超声水浴中，剧烈搅拌下缓慢滴加氨水至ph为7。采用超声波分散一定时间，搅拌直至用饱和bacl2检验滤液中无so■■，然后微波干燥后研磨煅烧获得疏松的nzt纳米粉体。 1.3 吸收范围测定 如要得到制备的纳米粉体对光谱的响应范围达到可见光区，可采用uv-vis分光光度法，对离子改性样品进行测试。扫描波长从200-600nm，每隔5nm测定一次吸光度。 1.4 光催化降解实验 光催化性能检测实验是以甲基橙为底物在攀枝花地区于9月下旬至10月上旬进行。在烧杯中加入配制好的一定质量浓度的甲基橙溶