Sn+取代对Ni系微波铁氧体材料性能的影响.doc

Sn4+取代对Ni系微波铁氧体材料性能的影响 袁红兰，冯 涛 （西南应用磁学研究说所，四川绵阳621000） 摘要：采用普通陶瓷工艺制备了Sn4+取代的Ni系尖晶石Ni1-a+xCuaSnxMnbFe2-b-2xO4微波多晶铁氧体材料，研究了材料性能随Sn4+取代量的变化。结果表明，铁磁共振线宽ΔH随Sn4+ 取代量x的增大先减小，后增大， 当x=0.1时，ΔH有最小值；饱和磁化强度MS、居里温度Tc随取代量x的增大单调降低，在x＝0.1时不存在拐点。初步分析了各向异性线宽ΔHa和气孔致宽ΔHp对ΔH的贡献，得出ΔH先降低而后增大是由各向异性线宽ΔHa所致。 关键词：尖晶石铁氧体；Sn4+取代；饱和磁化强度； 铁磁共振线宽；介电损耗；居里温度c Effects of Sn4+ substitution on the Magnetic Properties of microwave Ni Ferrites YUAN Hong-lan, FENG Tao Southwest Institute of Applied Magnetics, Mianyang 621000, China Abstract: , Sn4+-substituted microwave spine ferrite NiSn: Ni1-a+xCuaSnxMnbFe2-b-2xO4. was prepared by traditional ceramic processing, and the dependence of material properties on the substitution content was analyzed. The experiment results showed that,with inceeasing the Sn4+ content , ferromagnetic resonance linewidth ΔH decreases fistly and then increases with a minimum value at x=0.1.For saturation magnetization MS and Curie temperature Tc,there are no inflexions at x=0.1 and they go down with x. The contribution of anisotropy linewidth ΔHa and pore-induced ΔHp to ΔH was analyzed, coming to a conclusion that the first increase and then decrease of ΔH results from anisotropy linewidth ΔHa Key words: spine ferrite; saturation magnetization; ferromagnetic resonance linewidth; dielectric loss ;Curie temperature 引言 微波多晶铁为线宽温数Ni系微波铁氧体材料时，通常采用Sn4+取代降低饱和磁化强度MS，而不采用Al3+取代。Sn4+取代在降低Ms的同时也降低了ΔH，而Al3+取代虽降低了Ms却使ΔH相应增大 [1] 。 本文具体讨论Sn4+取代的Ni系微波铁氧体材料的性能，分析了饱和磁化强度Ms、铁磁共振线宽ΔH、介电损耗tg((、居里温度TC与Sn4+取代量之间的关系。 实验 微波铁氧体材料采用普通陶瓷工艺制备。用分析纯原材料Fe2O3、SnO2、MnCO3、CuO、NiO按照分子式Ni1-a+xCuaSnxMnbFe2-b-2xO4（0≤x≤0.2，a、b为小于0.1的固定值）进行配料。将配好的原材料放入滚动球磨机，加入酒精作弥散剂进行一次球磨，球磨5h后烘干，过30目筛。将筛好的粉料在950℃下预烧，保温4h。预烧料二次球磨24h后烘干。将二次球磨料按料重的10%加入浓度8%的聚乙烯醇作黏合剂造粒成型。将成型好的样品放入箱式炉中在1200℃下烧结4h，随炉冷却。用烧结好的样品制备成φ0.9mm、φ1.5mm的小球及φ1.6mm×25mm的圆棒，进行参数测量。 用排水法测量材料的表观密度ρapp，用环称测量在800 kA/m外加稳恒磁场下样品的比磁化强度σs和居里温度TC，由σs和密度计算出材料的饱和磁化强度MS