外文翻译--Fe-Fe3B-Y2O3纳米复合材料在千兆赫范围内的电磁微波吸收性能.docVIP

外文原文： Electromagnetic wave absorption properties of a-Fe/Fe3B/Y2O3nanocomposites in gigahertz range Jiu Rong Liu, Masahiro Itoh, and Ken-ichi Machidaa) a Collaborative Research Center for Advanced Science and Technology Osaka University, 2-1 Yamadaoka, Suita, Osaka 565-0871, Japan (Received 24 February 2003; accepted 8 September 2003) Abstract: Nanocomposites a-Fe/Fe3B/Y2O3 were prepared by a melt-spun technique, and the electromagneticwave absorption properties were measured in the 0.05–20.05 GHz range. Compared witha-Fe/Y2O3 composites, the resonance frequency (fr) of a-Fe/Fe3B/Y2O3 shifted to a higher frequency range due to the large anisotropy ?eld (HA) of tetragonal Fe3B (~0.4 MA/m). The relative permittivity () was constantly low over the 0.5–10 GHz region, which indicates that the composite powders have a high resistivity (). The effective electromagnetic wave absorption (re?ection loss -20 dB) was obtained in a frequency range of 2.7–6.5 GHz on resin composites of 80 wt% a-Fe/Fe3B/Y2O3 powders, with thickness of 6–3 mm, respectively. A minimum re?ection loss of -33 dB was observed at 4.5 GHz with an absorber thickness of 4 mm. ? 2003 American Institute of Physics. [DOI: 10.1063/1.1623934] Keywords: Nanocomposites a-Fe/Fe3B/Y2O3; Electromagnetic; Absorption performance 1. Introduction Recent employment of communication devices using the electromagnetic wave range of 1–6 GHz, (e.g., mobile telephones, intelligent transport systems, electronic toll collection systems, and local area network systems)has rapidly expanded. Therefore, serious electromagnetic interference problems have worsened. Concern for these problems has prompted the study of electromagnetic wave absorbing materials with antielectromagnetic interference coatings, self-concealing technology, and microwave darkrooms for the civil and military applications. The complex permeability () and permittivity() of materials determine the re?ection and attenuation characteristics of the electromagnetic