越南松邦4水电站大坝碾压混凝土温度控制施工设计.docVIP

越南松邦4水电站大坝碾压混凝土温度控制施工设计 　　摘要：RCC为脆性材料，其抗拉强度大约只有抗压强度的1/10,混凝土的抗拉变形能力很弱。但随着混凝土水化作用的增加，内部的水化热温度持续上升，将与混凝土表面产生较大的内外温差，这样混凝土表层可能会在拉应力的作用下产生裂缝。通过进行合理的温控措施施工设计，越南松邦4水电站大坝碾压混凝土温度得到了有效控制。 　　关键词：越南松邦4水电站；碾压混凝土；水化热；内外温差；温度控制 　　Abstract: RCC as brittle material, its tensile strength is only about 1/10 of the compressive strength, the tensile deformation of concrete is very weak. But with the increase of hydration of concrete, the internal heat of hydration temperature rising, will have a larger temperature difference between inside and outside, and the concrete surface, concrete surface may be cracks u