典型工业齿轮用渗碳钢热处理畸变特性的研究.pdfVIP

第九次全国热处理大会论文集(2007年9月大连) 典型工业齿轮用渗碳钢热处理畸变特性的研究 顾 敏，李宝奎，王爱香，赵少甫，许鸿翔，朱全意 (郑州机械研究所，河南郑州450001) 摘要：采用正交试验方法，研究了锻造比、预处理、渗碳温度、碳势、淬火温度及预热等材料与热处理工艺因素对20CrMnMo、 钢的淬透性以及淬透性对畸变的影响。针对四种渗碳钢的畸变特性，可通过优化的工艺参数较好地控制其畸变。 关键词：渗碳淬火；热处理畸变；齿轮钢；正交试验 ontheHeatTreatmentDistortionCharacteristicsofthe Study Typical and GearSteel Hardening GUMin，LI Shao—fu，XU Bao—kui，WANG Ai-xiang，ZHA0Hong—xiang．ZHUQuan—yi ResearchInstituteofMechanical He’nan (Zhengzhou Engineering，Zhengzhou450001，China) Abstract：Effectsofmaterialand factors technologyincludingforgingratio，pre—treatment，carburizing and ontheheattreatmentdistortion potential，quenchingtemperaturepreheating，etc four kindsof studied test．The steelwere ofthe steelwasStudied typical industrygear byorthogonalhardenabilitycarburizing by test．Theinfluenceof onthedistortionwasalso tothedistortioncharacteristicsofthefour Jominy hardenability Studied．According kindsof distortionwouldbecontroled via carburizingsteel，the preferablyoptimizedtechnological parameters． and treatment test Keywords：carburizinghardening；heatdistortion；gearsteel；orthogonal 对于承受重载、冲击和复杂应力的齿轮，要求具 有耐磨、抗表面接触疲劳和抗弯曲疲劳等综合性能。 目前在高参数硬齿面齿轮制造中，渗碳淬火工艺是最 过不同的锻造工艺进行锻造，其中一批预处理方式 主要的表面强化方式。但其存在的突出问题是齿轮的 为正火，另一批预处理方式为调质。然后经过车削 畸变。齿轮的畸变不仅使后续磨削量增加，提高生产 加工成标准端淬试样和线切害UJJn工成畸变试样(如 成本，而且还影响齿轮的承载能力和使用性能。本文 图1所示)。端淬试样进行末端淬火试验测定钢的淬 选用工业齿轮中常用渗碳钢20CrMnMo、20CrNi2Mo、 透性，畸变试样在108KW井式气体渗碳炉中进行渗 20Cr2Ni4、17CrN