510L 热轧带钢极限规格的生产工艺优化研究 ·1 · 510L 热轧带钢极限规格的生产工艺优化研究 1 1 1 1 1 2 赵启帆 曾 兢 肖 亚 向浪涛 汪 涛 罗云波 （1. 重钢股份有限公司钢研所，重庆 401220; 2. 重钢股份有限公司热轧薄板厂，重庆 401220 ） 摘 要 本文针对重钢1780 生产线510L 极限规格的热轧带钢成材率较低进行分析研究，对510L 极限规格的热轧 带钢进行生产工艺的优化设计，有效提高了该产品的成材率，并将解决方案纳入标准手册。 关键词 510L 成材率 优化工艺 方案 The Optimization Process Study of 510L Hot Rolling Steel Strip of Critical Size During Production Zhao Qifan1 Zeng Jing1 Xiao Ya1 Xiang Langtao1 Wang Tao1 Luo Yunbo2 (1.Iron and Steel Research Institute of Chongqing Iron Steel Co., Ltd., Chongqing, 401220; 2.Hot Rolling Plate Factory of Chongqing Iron Steel Co., Ltd., Chongqing, 401220) Abstract In this paper, as metallic consumption of 510L hot rolling steel strip of critical size was too much ,which is analyzed by us. thus we optimize the production process of 510L hot rolling steel strip of critical size, Through changing the speed of rolling mill.adjusting the load of mill, we reduce the metallic consumption of 510L steel strip availably,the solution will be brought into the standard of operating. Key words 510L steel strip, metallic consumption, optimization process, solution 1 研究背景 从2011 年 3 月份开始，重钢 1780 生产线开始进行510L 热轧带钢的小批量生产，主要规格为：厚度 5~8mm，宽度 1250/1270。从该规格510L 热卷实物质量来看，钢卷厚度、宽度偏差受控，卷形及外形质量 良好，力学及工艺性能均高于标准要求，从用户使用情况来看，产品加工成型性能良好，综合来讲,产品开 发取得阶段性成功。2011 年9 月，根据用户需求，公司继续对3.0mm 及以下厚度510L 极限规格热轧带钢 进行试生产，截至2012 年4 月，510L 极限规格产品共生产3 次，但轧成率、成材率偏低，其中综合轧成率 76.4%，成材率87.53%，远远低于同规格其他产品指标情况。鉴于此，为控制薄规格510L 轧废量、提升成 材率指标，需要对510L 极限规格的生产工艺进行优化研究。 2 510L 生产工艺流程 2.1 炼钢生产工艺流程 510L 热轧带钢成分设计思路采取在Q345 低合金钢基础上降C，控Si、控P、S 并适当添加微合金元素 赵启帆, 男, 本科, 助理工程师, 从事金属材料生产工作, qifanzhao@163.com ·2 ·