板坯表面质量及其标准的分析与研究.pdfVIP

板坯表面质量及其标准的分析与研究 ·1 · 板坯表面质量及其标准的分析与研究 1 1 1 2 彭洪宇 潘咏忠 廖 明 王 雨 （1. 重庆钢铁股份公司钢研所, 重庆 400084; 2. 重庆大学, 重庆 400044 ） 摘 要 通过对重钢新区铸坯表面缺陷类型、分布与发生频率的调查分析，以及对带缺陷铸坯的跟踪轧制试验，分 析并探讨典型铸坯表面缺陷在轧制过程中的演化行为。在以上试验的基础上，制定出重钢新区在当前轧制工艺条件 下的铸坯清理新标准，达到降低工人清理量，实现部分铸坯带缺陷轧制的目标。 关键词 表面质量 缺陷类型 带缺陷轧制 清理标准 The Analysis and Research of Slab Surface Quality and Its Standard Peng Hongyu1 Pan Yongzhong1 Liao Ming1 Wang Yu2 (1. Iron and Steel Research Institute of Chongqing Iron and Steel Co.,Ltd., Chongqing, 400084; 2. Chongqing University, Chongqing, 400044) Abstract Types, distribution and frequency of slab surface defect were analyzed for chongqing steel in this paper. through pre-productions of casting billets with defects its actions in rolling process were discussed and analyzed ．Based on the experiments new standard were formulated under current rolling process to reduce manual working，new production target was archived. Key words surface quality, defects type, rolling slab with detects, standard 1 前言 连铸坯表面质量不仅影响铸坯乃至钢板质量，而且还对连铸生产及钢-轧界面铸坯送转及生产产生不利 影响。通过对铸坯进行的带缺陷轧制的试验，实现部分铸坯带缺陷轧制的工艺，可以减轻铸坯清理耗时、耗 工和场地占用，提高经济效益。同时，通过铸坯带缺陷轧制的试验研究，摸清新区铸坯各类缺陷对轧后钢板 质量的影响，制定新区铸坯缺陷清理新标准，减轻铸坯清理量，并为实施铸坯热送热装工艺制定铸坯判定或 放行制度提供依据。 2 试验内容及方法 研究在重钢现行生产工艺条件下，铸坯主要表面缺陷的类型、分布与发生频率。现场确认铸坯缺陷类型， 测量铸坯缺陷深度、大小及在铸坯上的相对位置。通过对带缺陷铸坯做标记以跟踪轧制钢板对应位置的质量， 从而得到各种缺陷对在不同压缩比轧制后钢板质量的影响。分析并探讨典型铸坯表面缺陷在轧制过程中的演 化行为。在此基础上，制定重钢新区在当前轧制工艺条件下的铸坯清理新标准，达到降低工人清理量，实现 部分铸坯带缺陷轧制的目标。 ·2 · 第九届中国钢铁年会论文集 3 试验结果与分析 各类缺陷所占比例如图 1 所示。各类缺陷试验结果见表 1。 凹陷 裂纹