2.25Cr—1.0Mo钢连铸过程高温热塑性研究.pdfVIP

2．2scr一1．0Mo钢连铸过程高温热塑性研究 郭爱民袁伟霞 袁泽喜宋新莉 (武汉钢铁集团公司) (武汉科技大学) 摘要本研究采用G[eebie 2000热应力／应变模拟试验机，对2．2scr—l，OMo铜连铸过程的高温热塑 性进行了测试分析．探讨丁钢中添加微量元索硼和磷对高温热塑性的影响规律。研究表明：微量硼的器加显著 推迟丁先共析铁索体的析出，改善丁钢的高韫塑性t磷在奥氏体晶界产生丁严重的非平衡偏聚．使钢的高温热 塑性降低。采用俄歇谱仪测定表明，磷在晶界的偏聚量可达乎均成分的30倍；而在钢中添加微量硼，可与磷产 生交互作用，有利于抑制磷在晶界的非平衡偏聚．从而显著提高丁钢的热塑性，降低连锦过程的裂纹敏感性。 关键词连锦热塑性晶界偏聚2．25cr一1．OMo钢 Researchon Temperature High Steel of2．25Cr一1Mo Continuous During Casting Weixia Yuan Xinli GuoAttain，Yuan Zexi，Song (WuhanIronanaSteel ofScienceand Corp．)(Wuhanuniversity Technology) group Abstra!Thismeasureandtests of2-25cr一1MoSteel paper hjghtemperaturethermo--plasticity during theeffectlaw continuousonGteebleZ000thermalstress{strain testmachine，andexplounds casting simulating additionmicro——boronand tosteel0n results of hightemperaturethermo--plasticity．the micro--phosphorus the showsthatadditionofmiro—Boron of andimproves significantlydelaysprecipitatingpro--euteetoid[errit of inaustenite temperaturethemo—plasticity．severnon—equilibriumsegreationphosphorus crystal high resuLtsshowsthat amountof boundarymakehightemperaturethermo