-　　　　PTCA (PART :A PH YS.T EST .)　　　　2007 43 10 ———第五讲　金属材料与零件的表面完整性与疲劳断裂抗力间的关系 (, 100095) 　:论述了金属材料/零件的表面完整性与其疲劳断裂抗力之间的关系。试 结果表明, 表 面完整性中的残余应力、组织结构与表面粗糙度这三个因素对疲劳断裂抗力是最有影响力的三 个 因素。 :表面完整性;组织结构;残余应力;疲劳断裂抗力 :TB302.3　　　:A 　　　:1001-4012(2007)10-0535-05 BASIC KNOWLEDGE OF RESIDUA L ST RESS DETERMINATION ———LECTU RE No.5　REVIEW ON T HE RELATIONSHIP BETWEEN SU RFACE INTEGRITY AND FATIGUE FRACT URE RESISTANCE OF METALLIC M AT ERIA LS AND COMPONENTS WANG Ren-zhi (I stitute of Aero autical M aterials, Beiji g 100095, Chi a) The relatio ship betwee surface i tegrity (SI)of metal materials a d fatigue f racture resista ce Abstract: (FFR)are discussed.The experime ts have bee show that the three factors of residual stress microstructure as w ell as surface rough ess i cludi g i the all factors of SI have most i flue ce o the FFR. Keywords:Surface i tegrity;Microstructure;Residual stress;Fatigue fracture resista ce , /; 0 　 、 ( , :① ), (Microstructure, MS ), , 。, /(Fatigue , fracture resista ce, FFR), ;② (Plastic de- (Surface i tegrity, SI)。 formed structure, PDS );③ , , / (Delutio of alloyi g eleme t, DAE) , (σw ) (Pe etratio of exter al, DEE );④ 。 (Residual stress, RS )。 : 20 ～200 ℃, / , (Sur- , face rough ess, SR)。 R a () :※※ :2007-06-18 ※。 :(1932-), , 。 (600 ～750 ℃),