银钯%2fC7701冷复合工艺的研究.pdfVIP

11复合材料 银钯/C7701冷复合工艺研究 汪建胜，吴保安，李国纲，潘成刚 （重庆仪表材料研究所，400700） 摘 要:本文主要研究了基带C7701的状态、变形量以及复合速度和热处理方式等对C7701与银钯冷复合带 材表面质量、硬度、牢度及带材厚度的影响。研究结果得出：在一定的润滑条件下，以3.0m/min的复合速 度进行热处理基带 C7701与银钯冷复合，复合后进行 750~650℃可控气氛热处理，可生产鱼鳞状较少，硬 度达到HV160，不裂边，复合牢度可靠，厚度为0.08mm~0.035mm的银钯/C7701冷复合带材。 关键词：冷复合，银钯 中图分类号:TM205. 1 The technology study of Silver-Palladium/C7701 Cold composite Wang-Jiansheng,Wu-Baoan,Li-Guogang,Pan-Chenggang （Chongqing Instrument Materials Research Institute, Chongqing?Beibei,400700 ） Abstracts: This paper mainly studies the influences of the base state with C7701,deformation, composite rate and the heat treatment methods to the surface quality, hardness, fastness and thickness of C7701. The result show that if having the certain lubrication conditions ,3.0m/min composite ,750-650℃ heat treatment, we can get the less scaly , Hv160,not crack side ,composite fastness reliable ,and with 0.08mm~0.035 thickness C7701 Silver-Palladium cold composite strip. Keywords: Cold composite; Silver -Palldium, 引言 直流微电机换向器及电刷用的镶嵌复合金属材料是新型电接触材料,是以廉价金属无氧 铜、黄铜及锌白铜为基材,通过特殊的复合方法在其上镶嵌一条或多条贵金属,并通过后续工 序加工,进一步提高其结合强度、表面致密度、导电、导热、耐磨及抗氧化性能。选用这种 材料的换向器及电刷具有寿命长、磨损量小、转速稳定及噪声低等优异特性。 AgPd/C7701是目前常用的电刷材料之一，由于银钯具有良好的电接触性能被用作电刷材 料的电接触部分，而C7701而由于弹性好及耐磨性强、耐腐蚀性强、导电性高作为基材部分。 目前应用于微电机换向器和电刷用的贵/廉复合材料的生产方式主要有两种，一种是可控 气氛热复合，一种是室温固相复合。由于可控气氛热复合在复合AgPd/C7701的过程中会发生 基带开裂，贵金属AgPd表面有一层鱼鳞状，导致产品的成品率较低，贵金属表面不好。我们 汪建胜,工程师（WJSCZR2010@163.COM） 11复合材料 拟用室温固相复合的方式来生产，解决在复合过程中的基带裂边和贵金属表面无鱼鳞状 的产品。 1工艺研制 直流微电机电刷用镶嵌复合材料的主要工艺为: 贵金属真空熔炼 贵金属准备 室温固相复合 基带刨槽准备 包装 分条 表面处理 精轧 扩散退火 图1直流微电机电刷用镶嵌复合材料的主要工艺 1.1贵金属制造