本 科 毕 业 设 计 (论 文) VAc/BA/AA三元无皂乳液共聚的研究 Study on Emulsifer -free Emulsion of VAC /BA/AA 2011 年 6 月 毕业设计（论文）中文摘要 VAc/BA/AA三元无皂乳液共聚的研究 摘 要：采用无皂乳液聚合方式，以醋酸乙烯酯、丙烯酸丁酯、 丙烯酸为单体，过硫酸铵为引发剂制备三元共聚物，探讨了丙烯酸用量、引发剂用量对乳液的转化率、耐水性、含固率、凝胶率以及粒径分布的影响规律。对实验过程的各种实验现象及数据进行了详细的记录 毕业设计（论文）外文摘要 Study on Emulsifer -free Emulsion of VAC /BA/AA Abstract: The latex particles of VAC /BA/AA were prepared via an emulsifier-free emulsion copolymerization using KPS as an initiator and VAc,BA,AA as monomers .The influence of initiator and functional monomer (AA) on the conversion rate, absorption rate , solid content, gel rate and particle size distribution was studied. In the course of study, experimental phenomena and data are recorded in details, test of infrared spectrum, particle size distribution and other related experiment are conducted to explore the property of the polymer. Keywords: emulsifier-free emulsion copolymerization; polyvinyl acetate(VAc); acrylic acid(AA); ammonium persulfate (APS); preparation  目 录 1 引言 1 1.1 乳液聚合 1 1.2 聚醋酸乙烯酯乳液的研究与现状 1 1.3 无皂乳液 2 1.4 无皂乳液的常用聚合方法 3 1.5 无皂乳液聚合的应用 4 1.6 无皂乳液法制聚醋酸乙烯酯乳液的研究 4 1.7 论文的主要研究内容与意义 4 2 实验部分 6 2.1 实验装置及仪器 6 2.2 实验药品 6 2.3 实验原理及步骤 7 2.4 实验过程及现象进行记录 9 2.5 性能测试 10 3 数据分析与讨论 12 3.1 乳液外观目测 12 3.2 红外表征 12 3.3 凝胶率 13 3.4 含固率 14 3.5 转化率 15 3.6 耐水性 16 3.7 机械稳定性 17 3.8 稀释稳定性 17 3.9 冻融稳定性 17 3.10 高温稳定性 17 3.11 粒径分布 17 结 论 20 致 谢 21 参 考 文 献 22 1 引言 1.1 乳液聚合 1.1.1 乳液聚合特点 乳液聚合是高分子合成中的一种常用合成方法，一般以水为溶剂，液态的乙烯基单体或二烯烃单体在乳化剂的存在与机械搅拌的作用下分散于水中成为乳状液，并由引发剂引发聚合反应。 乳液聚合与其他自由基聚合反应方法相比有着独特的优点。通常，烯类单体的聚合反应放热量都很大，在生产过程中，不易控制排热，不仅影响了产品的品质，还易造成安全隐患。但是，对乳液聚合过程来说，聚合反应发生水相的乳胶粒眼。在烯类单体的自由基聚合中，乳液聚合可以将二者统一起来，即既有高的反应速率，又可得到高分子量的聚合物，在水相中分解成自由基扩散到胶束或乳胶粒中，在其中引发聚合。乳液聚合自由基。Fitch提出了无皂乳液的均相成核机理，后来Goodwin,Hansen和Vgelastad等人对其进行了完善[12]。他们认为，聚合反应最初是在水相中进行的，引发剂首先溶于水中生成自由基，与水相中的单体分子发生聚合并进行链增长。当活性链增长至临界链长时，便自身缠结，从水相析出形成基本粒子。这些基本粒子由于表面电荷密度较低，粒子之间的静电排斥力不足以使粒子稳定再进一步聚合最终形成稳定的乳胶粒[13]。 (2) 齐聚物胶束成核机理 Goodwall等人在进行无皂法制备苯乙烯乳液的过程中用过硫酸钾做引发剂并提出了齐聚物胶束成核机理。他们认为