薄板坯连铸连轧工艺生产薄规格高强钢的研究现状 ·1 · 薄板坯连铸连轧工艺生产薄规格高强钢的研究现状 宋 畅 马玉喜 陶军晖 刘志勇 （武汉钢铁（集团）公司研究院，武汉 430080 ） 摘 要 薄板坯连铸连轧工艺在实现“ 以热代冷”及“ 以薄代厚”方面较常规热轧具有独到的优势。本文主要概述了国 内外代表钢厂生产屈服强度700MPa 级高强钢的现状，包括其成分设计思路、组织性能及强化机理，分析了薄板坯 连铸连轧工艺生产高强钢的优势，提出了其关键技术及发展趋势。 关键词 薄板坯连铸连轧 高强钢 薄规格 微合金化 Status of Producing Thin Strip with High Strength by TSCR Song Chang Ma Yuxi Tao Junhui Liu Zhiyong (Research and Development Center of WISCO, Wuhan, 430080) Abstract Thin Slab Controlled Rolling(TSCR) has particular advantages in substituting hot rolled strip for cold rolled strip and substituting thin strip for thick strip. This article mainly summarized the status of producing high strength steels of 700MPa at home and aboard, including chemical composition design, microstructure, property and strengthening mechanism. Moreover, the advantages of producing high strength steels by TSCR process were analysed. Finally, the key technologies and development trend of producing high strength steels by TSCR were presented. Key words thin slab controlled rolling, high strength steel, thin strip, microalloying 随着世界能源、资源和环境保护问题日趋严峻，钢铁材料实现高强度、轻量化及节能降耗成为迫切需要。 目前，屈服强度700MPa级高强钢主要分为高强度耐候钢和冷成形用高强钢。冷成形用高强钢主要用于对强 度、成形性和焊接性有较高要求的工程机械、交通运输和车辆制造行业[1] 。薄规格高强钢的使用，不仅可使 制造车辆部件、起重运输设备的企业降低钢材使用量及生产成本，同时降低用户油耗成本，减少污染物排放， 从而实现生产厂、用户及社会的三方共赢，因此薄规格高强钢具有很大市场潜力。 薄板坯连铸连轧（TSCR ）生产线自1989年建成后，世界各国纷纷引进该生产线，世界上已投产和在建 的TSCR生产线已有71条，年生产能力超过1亿吨，其中CSP线39条，占薄板坯连铸机总产能的50% 以上。我 国已建成13条生产线，其中CSP生产线7条，年生产能力达3000多万吨。各大钢厂生产实践表明，薄板坯连 [2] 铸连轧工艺生产薄规格的高强钢具有独到的优势 。 本文主要概述了国内外代表钢厂生产屈服强度700MPa 级高强钢的现状，包括其成分设计思路、组织性 能及强化机理，分析了薄板坯连铸连轧工艺生产高强钢的优势，提出了其关键技术及发展趋势。 1 薄板坯连铸连轧工艺生产薄规格高强钢的现状 目前，世界上生产屈服强度700 MPa 级薄规格高强钢的主要有以下三种产线：一是利用传统热轧产线， 宋畅, 女, 硕士, 助理工程师, 从事高强钢开发, so