JB 4726-2000 英文版 压力容器用碳素钢和低合金钢锻件.pdfVIP

本英文版为内部资料，仅供参考，以中文 版为准。 The Chinese version of standards has precedence to their English translations which are only for internal reference. JB 4726 – 2000 压力容器用碳素钢和低合金钢锻件 Carbon and Low-alloy Steel Forgings for Pressure Vessels — 1 — Preface This standard is the revised version of JB 4726 – 1994. This standard has made following changes based on the comments obtained since the implementation of JB 4726 – 1994, the domestic development of new steel grade and reference of the recent international similar standards: 1 15MnV, currently not used, has been canceled; 2 Moderate temperate hydrogen resistant steel 14CrlMo has been added; 3 Phosphorus and sulfur contents have been decreased widely based on the domestic advanced smelting level so as to reach the international advanced level; 4 0 ℃ impact test shall be used for 16Mn, 20MnMo, 20MnMoNb forgings instead of 20 ℃ impact test, so as to meet the requirement of pressure vessel product standard; 5 Considering the safety of pressure vessels stipulations in appendix B have been added for each steel grade in this standard, JB 4726 – 1994 shall be null since the implementation date of this standard. Appendix A and Appendix B of this standard are the standard appendixes. This standard is put forth by The National Pressure Vessels Standardization and Technical Committee. This standard belongs by right to the Manufacturing Sub-committee of the National Pressure Vessel Standardization and Technical Committee. Responsible drafting unit of this standard: Hefei General Machinery Research Institute, China General Machinery and Engineering Company, Wuhan Heavy-duty Casting and Forging Works. Main drafters of this