This formulation is shown in one of documents from INDSPEC.?Resorcinol or B-20-S is added?at step 2.?Generally，resorcinol cant be added in step1 due to its significant fuming under?temperature as high as to 160-180 Usually, B-20-S is used in some skim compounds.?One of?our customers told us that when mixed with B-20-S,?the skim?compound got blooming.?We cant see the real conditions of blooming rubber, so its not confirmed whether the blooming is caused by addition of B-20-S.?Whats your comment?? From some papers drawn by compounders, in the subsequent processing of skim compound, especially when calendering, compound?mixed with resorcinol still has problem of fuming. We are confident that B-20-S can resolve this upsetting. Whats your recommendations in the subsequent process? Additionally, we dont know how long B-20-S could be stored in normal conditions? 由于橡胶在一段混炼的温度有时可高达160-180℃，间苯二酚在这个温度下会产生显著的冒烟现象，所以在通常情况下，间苯二酚或B-20-S一般在二段混炼时加入；但B-20-S不会产生冒烟问题，可否在一段混炼时加入？ 在胶料的后续加工过程中，特别是在压延过程中，用间苯二酚配合的胶料仍然会产生冒烟，我们相信B-20-S可以解决这个问题；但有用户在使用B-20-S时，发现胶料有喷霜现象，请问产生喷霜的可能原因是什么？ 请问B-20-S在通常情况下存储时间有多长？ 1.? Penacolite??Resin B-20-S can be added to the first mix stage without significant fuming.? However we have seen slightly higher?cured modulus if it is added in a later mix stage.? Adhesion is not affected by which mix stage B-20-S is added.? A B-20-S containing compound should not fume during calendering, however it might be slightly higher in Mooney viscosity than a resorcinol compound so other compound adjustments might be necessary if they cannot tolerate increased Mooney viscosity.? 1.Penacolite 树脂B-20-S可以在一段混炼时加入，而不会出现显著的冒烟现象。在后续混炼阶段加入时，硫化胶的模量会稍微提高。胶料的黏合力*不受B-20-S加入阶段的影响。与含有纯间苯二酚的胶料相比，用B-20-S混合的胶料其门尼粘度会稍微增加，在压延时不会出现冒烟现象；如果用户不希望（用B-20-S混合的胶料）门尼粘度增加，那么就有必要做其它混配合方面的调整。 2.? Penacolite Resin B-20-S does not usually bloom.?Several things could be happening: ????a.? Because B-20-S does increase Mooney viscosity, they might be running?a higher temperature during mixing or calendering, whic